Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Characteristics
- Medium high impact
- Injection molding
- High flow for process
- UL 1/16” V-0
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Injection Molding
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Moisture Absorption Equilibrium (23°C/50% RH) | max. 0.3 | wt% | ASTMD570 |
| Mold Shrinkage (60×60×2mm SFlow) | max. 0.4 | wt% | ASTMD955 |
| Rockwell Hardness (23°C, R-scale) | 102.0 | R-scale | ASTMD785 |
| Value | Units | Test Method / Conditions | |
| Elongation at Break (23°C, 5 mm/min) | 20.0 | % | ASTMD638 |
| Flexural Modulus (23°C, 2.8 mm/min) | 22000.0 | kg/cm2 | ASTMD790 |
| Flexural Yield (23°C, 2.8 mm/min) | 600.0 | kg/cm2 | ASTMD790 |
| Izod Impact Strength (23°C, 1/4” Notched) | 17.0 | kg-cm/cm | ASTMD256 |
| Izod Impact Strength (23°C, 1/8” Notched) | 20.0 | kg-cm/cm | ASTMD256 |
| Tensile Strength at Break (23°C, 5 mm/min) | 300.0 | kg/cm2 | ASTMD638 |
| Tensile Strength at Yield (23°C, 5 mm/min) | 380.0 | kg/cm2 | ASTMD638 |
| Value | Units | Test Method / Conditions | |
| Heat Distortion Temperature (Unannealing 1.8MPa) | 77.0 | °C | ASTMD648 |
| RTI Elec (1.5 mm) | 60.0 | — | UL 746 |
| RTI Elec (3.0 mm) | 60.0 | — | UL 746 |
| RTI Elec (6.0 mm) | 60.0 | — | UL 746 |
| RTI Imp (1.5 mm) | 60.0 | — | UL 746 |
| RTI Imp (3.0 mm) | 60.0 | — | UL 746 |
| RTI Imp (6.0 mm) | 60.0 | — | UL 746 |
| RTI Str (1.5 mm) | 60.0 | — | UL 746 |
| RTI Str (3.0 mm) | 60.0 | — | UL 746 |
| RTI Str (6.0 mm) | 60.0 | — | UL 746 |
| Vicat Softening Temperature (50°C/hr , 1 kg load) | 94.0 | °C | ASTMD1525 |
| Value | Units | Test Method / Conditions | |
| Arc Resistance | PLC 7 | — | ASTM D495 |
| Arc Tracking Rate (0.062 inch above) | 4.2 | in/min | UL-746A |
| Comparative Tracking Index | PLC 2 | — | UL 746 |
| Dielictric Strength | 22.0 | KV/mm | ASTM D149 |
| High Amp Arc lgnition (1.5 mm) | PLC 4 | — | UL 746 |
| High Amp Arc lgnition (3.0 mm) | PLC 4 | — | UL 746 |
| High Current Arc Ignition (0.062 inch above) | 10.0 | Arcs | UL-746A |
| High Voltage Arc Tracking Rate | PLC 0 | — | UL 746 |
| Hot Wire Ignition (0.062 inch above) | 57.0 | Secs | UL-746A |
| Hot-Wire Ignition (1.5 mm) | PLC 2 | — | UL 746 |
| Hot-Wire Ignition (3.0 mm) | PLC 1 | — | UL 746 |
| Relative Temperature Index (0.062 inch above) | 60.0 | °C | UL-746B |
| Volume Resistivity | 1.0E+16 | Ohm-cm | ASTM D257 |
| Value | Units | Test Method / Conditions | |
| Flame Rating (1.5 mm) | V-0 | — | UL 94 |
| Flame Rating (3.0 mm) | V-0, 5VA | — | IEC 60695-11-10,-20 |
| Flame Rating (6.0 mm) | V-0 5VA | — | IEC 60695-11-10,-21 |
| Value | Units | Test Method / Conditions | |
| Back Pressure | 50 - 70 | psi(Mpa) | — |
| Drying Temperature | 70 - 75 | °C | — |
| Drying Time | 2.0 - 4.0 | hr | — |
| Front Zone | 170 - 200 | °C | — |
| Injection Pressure | Moderate to Moderately high | — | — |
| Injection Speed | Moderate to Fast | — | — |
| Melt Zone | 165 - 175 | °C | — |
| Middle Zone | 180 - 210 | °C | — |
| Mold Temperature | 40 - 70 | °C | — |
| Nozzle | 190 - 220 | °C | — |
| Rear Zone | 170 - 200 | °C | — |
| Screw Speed | 30 - 100 | rpm | — |
| Value | Units | Test Method / Conditions | |
| Melt Volume Rate (200°C, 5kg load) | 5.0 | g/10min | ASTM D1238 |
| Melt Volume Rate (220°C, 10kg load) | 45.0 | g/10min | ASTM D1238 |
| Specific Gravity (23°C) | 1.17 | g/cm3 | ASTM D792 |
Regulatory & Compliance
- Certifications & Compliance