Properties
- Mechanical Properties
- Thermal Properties
- Rheological Properties
Value | Units | Test Method / Conditions | |
Tensile modulus at 23°C, 1 mm/min | 2025 | MPa | ISO 527-2 |
Flexural modulus at 23°C & 2 mm/min | 1900 | MPa | ISO 178 |
Flexural modulus at 23°C & 2 mm/min | 38 | MPa | ISO 178 |
Tensile strength at 23°C, 50 mm/min | 16 | MPa | ISO 527-2 |
Elongation at break at 23°C & 5 mm/min | 60 | % | ISO 527-2 |
Charpy impact 1eU at 23°C | 52 | kJ/m2 | ISO 179-1 |
Charpy impact 1eA at 23°C | 4 | kJ/m2 | ISO 179-1 |
Charpy impact 1eU at -40°C | 19 | kJ/m2 | ISO 179-1 |
Charpy impact 1eA at -40°C | 1.4 | kJ/m2 | ISO 179-1 |
IZOD impact 1eU at 23°C | 47 | kJ/m2 | ISO 180-1 |
IZOD impact 1eA at 23°C | 4.5 | kJ/m2 | ISO 180-1 |
IZOD impact 1eU at -40°C | 18 | kJ/m2 | ISO 180-1 |
IZOD impact 1eA at -40°C | 2.2 | kJ/m2 | ISO 180-1 |
Shore D | 68 | MPa | ISO 868 |
Value | Units | Test Method / Conditions | |
Vicat softening temperature at 50°C/h 10 N | 151 | °C | ISO 306 |
HDT-A (1,80 MPa) | 48 | °C | ISO 75 |
HDT-B (0,45 MPa) | 83 | °C | ISO 75 |
Value | Units | Test Method / Conditions | |
Melt flow index MFI at 230°C/ 2.16 kg | 24 | g/10 min | ISO 1133 |