EcoForte® PPH GF 30 100

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Glass Fiber

Polymer Name

Polypropylene Homopolymer (HPP)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

Halogen-free

Materials Features

Flame Retardant

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Printing & Packaging

Applications

Automotive & Transportation — Automotive

Other Automotive Applications

Building & Construction — Building Envelope & Roofing

Building & Construction — Building Materials

Other Building Materials,

Wall Panels

Printing & Packaging — Packaging

Other Packaging Materials

Plastics & Elastomers End Uses

Flexible Packaging,

Rigid Films,

Rigid Packaging,

Roofing Elements,

Wall Panels

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile modulus at 23°C, 1 mm/min	6910	MPa	ISO 527-2
Tensile strength at 23°C, 5 mm/min	91	MPa	ISO 527-2
Elongation at break at 23°C & 5 mm/min	2,9	%	ISO 527-2
Flexural modulus at 23°C & 2 mm/min	6150	MPa	ISO 178
Flexural modulus at 23°C & 2 mm/min	145	MPa	ISO 178
Charpy impact 1eU at 23°C	54	kJ/m2	ISO 179-1
Charpy impact 1eA at 23°C	12	kJ/m2	ISO 179-1

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat softening temperature at 50°C/h 10 N	167	°C	ISO 306
Vicat softening temperature at 50°C/h 10 N	143	°C	ISO 306
HDT-A (1,80 MPa)	152	°C	ISO 75
HDT-B (0,45 MPa)	161	°C	ISO 75

Typical Properties

	Value	Units	Test Method / Conditions
Density	1124	kg/m3	ISO 1183
Glass fibre content	30	%	Inhouse

Rheological Properties

	Value	Units	Test Method / Conditions
Melt flow index MFI at 230°C/ 2.16 kg	7	g/10 min	ISO 1133
Melt volume ratio MVR at 230°C/ 2,16 kg	7	cm3/10 min	ISO 1133