| Bayshore Resilience | 58 | % | Internal |
| Tensile modulus (1mm/min) | 55 | MPa | ISO 527-2/1A |
| Tensile strain at break (50mm/min) | 650 | % | ISO 527-2/1A |
| Flexural Modulus (-40°C) | 270 | MPa | ISO 178 |
| Flexural Modulus (100°C) | 26 | MPa | ISO 178 |
| Flexural Modulus (23°C) | 46 | MPa | ISO 178 |
| Hardness (15 sec) | 40 | Shore D | ISO 868 |
| Hardness (15 sec) | 92 | Shore D | ISO 868 |
| Izod Notched Impact Strength (-30°C) | NB | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (-40°C) | NB | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (23°C) | NB | kJ/m² | ISO 180/1A |
| Izod Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 180/10 |
| Izod Unnotched Impact Strength (30°C) | NB | kJ/m² | ISO 180/10 |
| Strain (Break) | 650 | % | ISO 527-1/-2 |
| Stress (10% Elongation) | 3.2 | MPa | ISO 527-1/-2 |
| Stress (100% Elongation) | 7.7 | MPa | ISO 527-11-2 |
| Ross flex | min. 1000000 cycles | — | Internal |
| Ross flex | min. 1000000 | cycles | Internal |
| Stress (300% Elongation) | 12.7 | MPa | ISO 527-1/-2 |
| Stress (50% Elongation) | 6.6 | MPa | ISO 727-1/2 |
| Stress (Break) | 21 | MPa | ISO 527-1/-2 |
| Tensile Stress (50% strain (50mm/min)) | 7 | MPa | ISO 527-2/1A |
| Tensile Stress (Break (50mm/min)) | 21 | MPa | ISO 527-2/1A |
| Tear strength (Die C, parallel) | 84.8 | kN/m | ISO 34-1 |
| Charpy Impact Strength (-30°C) | NB | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (23°C) | NB | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (-30°C) | NB | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (23°C) | NB | kJ/m² | ISO 179/16A |
| Flexural Stress (3.5% Strain) | 2 | MPa | ISO 178 |