- High viscosity basic PA6 grade.
- Suitable for small diameter monofilament applications.
Properties
- Physical Properties
- Thermal Properties
- Optical Properties
- Film Properties (PA Monolayer - Airblown Films)
Value | Units | Test Method / Conditions | |
Density | 1140 | kg/m3 | ASTM D 792 |
Value | Units | Test Method / Conditions | |
Melting temperature (10°C/min) | 215 | °C | ISO 11357-1/-3 |
Value | Units | Test Method / Conditions | |
Haze | 0.5 | % | ASTM D 1003 |
Gloss | 155 | - | ASTM D 2457 |
Value | Units | Test Method / Conditions | |
Melting Point | 217 - 221 | °C | ISO 11357-3 |
Crystallization Temperature (Tc) | 178 - 182 | °C | ISO 11357-3 |
Glass Transition Temperature (Tg) | 52 - 56 | °C | ISO 11357-3 |
Haze | 20 - 22 | % | ASTM D-1003 |
Gloss (at 60°) | 75 - 95 | % | ASTM D-523 |
Oxygen (T=23°C, RH=0%) | 20 - 22 | ml/m2.day | ASTM D-3985 |
Water Vapor (T=40°C, RH=90%) | 120 - 140 | g/m2.day | JIS Z-0208 |
Coefficient of Friction (Static) | 0.28 - 0.32 | — | ASTM D-1894 |
Coefficient of Friction (Dynamic) | 0.28 - 0.32 | — | ASTM D-1894 |
Tensile Strength at Yield | 36 - 40 | Mpa | ISO 527-3 |
Tensile Strength at Break | 90 - 100 | Mpa | ISO 527-3 |
Tensile Elongation at Break | 380 - 400 | % | ISO 527-3 |
Tensile Modulus | 700 - 800 | Mpa | ISO 527-3 |
Tear Load | 0.6 - 0.8 | N | ASTM D1922 |
Puncture Energy | 23 - 25 | mJ | JAS P-1019 |
Puncture Deformation | 7 - 8 | mm | JAS P-1019 |
Spencer Impact Energy | 700 - 800 | mJ | ASTM D3420 |
Flex Crack (Gelboflex) (at 23°C 1000 Cycles) | max. 40 | Holes/0,04m2 | Mil B-131C |
Flex Crack (Gelboflex) (at 5°C 100 Cycles) | max. 10 | Holes/0,04m2 | Mil B-131C |
Thermoforming Depth | max. 60 - 70 | mm | UBE METHOD |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Notes
- Equipment: 5 layers airblown line.
- Die: Diameter = 90 mm • Gap = 1,4 mm.
- Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
- PA layer delaminated for the tests.
- Layer thickness distribution: PE = 50μm, PA = 50μm,
- PE = 50μm (Total film thickness = 150μm).
- Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
- Film orientation: Blow-up ratio = 2,1 •
- Take-off speed = 6m min-1.
- Samples conditioning and testing conditions: T = 23ºC, RH = 50%.
- UBE Nylon Grades for Grass Timmer
Grades Types Line Strength Knot Strength Flexibility Heat Resistance Standard UBE Nylon 1030 B Suitable Suitable Suitable Exceptional