UBE Nylon 6434 FD12

1 of 97 products in this brand
UBE Nylon 6434 FD12 is a Polyamide 66/612 Copolymer polymer. It is processed by using film extrusion, blown film extrusion & extrusion methods.

Polymer Name: Polyamide 66/612 Copolymer

Processing Methods: Blown Film Extrusion, Extrusion, Film Extrusion

    Knowde Enhanced TDS

    Identification & Functionality

    Chemical Family
    Technologies

    Features & Benefits

    Labeling Claims
    Food legislation compliance
    • EC: Approved for indirect food contact & Approved for direct food contact.
    • FDA: Approved for indirect food contact & Approved for direct food contact.

    Applications & Uses

    Plastics & Elastomers Processing Methods
    Applications

    Suitable in outer layer for demanding applications requesting additional good slip properties.

    Properties

    Film Properties (PA Monolayer - Airblown Films)
    ValueUnitsTest Method / Conditions
    Melting Point184 - 188°CISO 11357-3
    Crystallization Temperature (Tc)131 - 135°CISO 11357-3
    Glass Transition Temperature (Tg)45 - 49°CISO 11357-3
    Haze2 - 4%ASTM D-1003
    Gloss (at 60°)120 - 140%ASTM D-523
    Oxygen (T=23°C, RH=0%)54 - 56ml/m2.dayASTM D-3985
    Water Vapor (T=40°C, RH=90%)130 - 150g/m2.dayJIS Z-0208
    Coefficient of Friction (Static)0.24 - 0.28ASTM D-1894
    Coefficient of Friction (Dynamic)0.24 - 0.28ASTM D-1894
    Tensile Strength at Yield23 - 27MpaISO 527-3
    Tensile Strength at Break115 - 135MpaISO 527-3
    Tensile Elongation at Break490 - 510%ISO 527-3
    Tensile Modulus450 - 550MpaISO 527-3
    Tear Load2.2 - 2.4NASTM D1922
    Puncture Energy33 - 35mJJAS P-1019
    Puncture Deformation10.5 - 11.5mmJAS P-1019
    Spencer Impact Energy850 - 950mJASTM D3420
    Flex Crack (Gelboflex) (at 23°C 1000 Cycles)max. 10Holes/0,04m2Mil B-131C
    Flex Crack (Gelboflex) (at 5°C 100 Cycles)0Holes/0,04m2Mil B-131C
    Thermoforming Depthmax. 90 - 100mmUBE METHOD

    Technical Details & Test Data

    Notes
    • Equipment: 5 layers airblown line.
    • Die: Diameter = 90 mm • Gap = 1,4 mm.
    • Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
    • PA layer delaminated for the tests.
    • Layer thickness distribution: PE = 50μm, PA = 50μm,
    • PE = 50μm (Total film thickness = 150μm).
    • Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
    • Film orientation: Blow-up ratio = 2,1 •
    • Take-off speed = 6m min-1.
    • Samples conditioning and testing conditions: T = 23ºC, RH = 50%.