Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Food legislation compliance
- EC: Approved for indirect food contact & Approved for direct food contact.
- FDA: Approved for indirect food contact & Approved for direct food contact.
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Suitable for deep drawing thermoforming applications.
Properties
- Film Properties (PA Monolayer - Airblown Films)
Value | Units | Test Method / Conditions | |
Melting Point | 184 - 188 | °C | ISO 11357-3 |
Crystallization Temperature (Tc) | 112 - 116 | °C | ISO 11357-3 |
Glass Transition Temperature (Tg) | 54 - 58 | °C | ISO 11357-3 |
Haze | 1 - 3 | % | ASTM D-1003 |
Gloss (at 60°) | 140 - 160 | % | ASTM D-523 |
Oxygen (T=23°C, RH=0%) | 47 - 49 | ml/m2.day | ASTM D-3985 |
Water Vapor (T=40°C, RH=90%) | 90 - 110 | g/m2.day | JIS Z-0208 |
Coefficient of Friction (Static) | 0.50 - 0.54 | — | ASTM D-1894 |
Coefficient of Friction (Dynamic) | 0.50 - 0.54 | — | ASTM D-1894 |
Tensile Strength at Yield | 26 - 30 | Mpa | ISO 527-3 |
Tensile Strength at Break | 115 - 135 | Mpa | ISO 527-3 |
Tensile Elongation at Break | 500 - 520 | % | ISO 527-3 |
Tensile Modulus | 600 - 700 | Mpa | ISO 527-3 |
Tear Load | 2.2 - 2.4 | N | ASTM D1922 |
Puncture Energy | 38 - 40 | mJ | JAS P-1019 |
Puncture Deformation | 10.5 - 11.5 | mm | JAS P-1019 |
Spencer Impact Energy | 850 - 950 | mJ | ASTM D3420 |
Flex Crack (Gelboflex) (at 23°C 1000 Cycles) | max. 70 | Holes/0,04m2 | Mil B-131C |
Flex Crack (Gelboflex) (at 5°C 100 Cycles) | max. 10 | Holes/0,04m2 | Mil B-131C |
Thermoforming Depth | max. 100 - 120 | mm | UBE METHOD |
Technical Details & Test Data
- Notes
- Equipment: 5 layers airblown line.
- Die: Diameter = 90 mm • Gap = 1,4 mm.
- Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
- PA layer delaminated for the tests.
- Layer thickness distribution: PE = 50μm, PA = 50μm,
- PE = 50μm (Total film thickness = 150μm).
- Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
- Film orientation: Blow-up ratio = 2,1 •
- Take-off speed = 6m min-1.
- Samples conditioning and testing conditions: T = 23ºC, RH = 50%.
- UBE Nylon Grades for Thermoforming
Grades Types Processability
(airblown)Thermoforming Optical
propertiesPuncture
resistanceFlexibility Functional UBE Nylon 6434 FD14 Exceptional Exceptional Exceptional Exceptional Suitable