UBE Nylon 6434 JI1

Identification & Functionality

Additives Included

Heat Stabilizer,

Impact Modifier,

Plasticizer (Unspecified)

Chemical Family

Polyamides

Polymer Name

Polyamide 66/612 Copolymer

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

Recyclable,

Sustainable

Materials Features

Cost Effective,

Heat Stabilized,

Impact Modified,

Low Emissions,

Plasticized,

Recyclable

Applications & Uses

Markets

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Industrial — Other Industrial Applications

Plastics & Elastomers End Uses

Film,

Industrial Film Applications

Plastics & Elastomers Processing Methods

Blown Film Extrusion,

Extrusion,

Film Extrusion

Properties

Film Properties (PA Monolayer - Airblown Films)

	Value	Units	Test Method / Conditions
Melting Point	182 - 186	°C	ISO 11357-3
Crystallization Temperature (Tc)	135 - 139	°C	ISO 11357-3
Glass Transition Temperature (Tg)	29 - 33	°C	ISO 11357-3
Haze	21 - 23	%	ASTM D-1003
Gloss (at 60°)	75 - 95	%	ASTM D-523
Oxygen (T=23°C, RH=0%)	94 - 96	ml/m2.day	ASTM D-3985
Water Vapor (T=40°C, RH=90%)	110 - 130	g/m2.day	JIS Z-0208
Coefficient of Friction (Static)	0.74 - 0.78	—	ASTM D-1894
Coefficient of Friction (Dynamic)	0.74 - 0.78	—	ASTM D-1894
Tensile Strength at Break	90 - 110	Mpa	ISO 527-3
Tensile Elongation at Break	480 - 500	%	ISO 527-3
Tensile Modulus	300 - 400	Mpa	ISO 527-3
Tear Load	5.0 - 5.2	N	ASTM D1922
Puncture Energy	25 - 27	mJ	JAS P-1019
Puncture Deformation	10 - 11	mm	JAS P-1019
Spencer Impact Energy	900 - 1000	mJ	ASTM D3420
Flex Crack (Gelboflex) (at 23°C 1000 Cycles)	0	Holes/0,04m2	Mil B-131C
Flex Crack (Gelboflex) (at 5°C 100 Cycles)	0	Holes/0,04m2	Mil B-131C

Technical Details & Test Data

Notes

• Equipment: 5 layers airblown line.
• Die: Diameter = 90 mm • Gap = 1,4 mm.
• Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
• PA layer delaminated for the tests.
• Layer thickness distribution: PE = 50μm, PA = 50μm,
• PE = 50μm (Total film thickness = 150μm).
• Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
• Film orientation: Blow-up ratio = 2,1 •
• Take-off speed = 6m min-1.
• Samples conditioning and testing conditions: T = 23ºC, RH = 50%.

Applications

Plasticized, impact modified and heat stabilized PA6/6.6/12 grade.