UBE Nylon 6434 MT1

Identification & Functionality

Chemical Family

Polyamides

Polymer Name

Polyamide 66/612 Copolymer

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

Recyclable,

Sustainable

Materials Features

Cost Effective,

Ease of Handling,

Excellent Strength,

Excellent Transparency Properties,

Good Flexibility,

Good Optical Properties,

Heat Resistance,

High Viscosity,

Light Weight,

Long Seal Life,

Low Emissions,

Recyclable,

Soft

Applications & Uses

Markets

Consumer Goods,

Industrial

Applications

Consumer Goods — Other Consumer Goods Applications

Industrial — Other Industrial Applications

Consumer Goods — Sports & Recreation

Composites End Use

Profiles

Plastics & Elastomers End Uses

Door Profiles,

Film,

Monofilaments

Plastics & Elastomers Processing Methods

Blown Film Extrusion,

Extrusion,

Film Extrusion

Applications

High viscosity soft PA6/6.6/12 grade.

Properties

Film Properties (PA Monolayer - Airblown Films)

	Value	Units	Test Method / Conditions
Melting Point	181 - 185	°C	ISO 11357-3
Crystallization Temperature (Tc)	127 - 131	°C	ISO 11357-3
Glass Transition Temperature (Tg)	41 - 45	°C	ISO 11357-3
Haze	4 - 6	%	ASTM D-1003
Gloss (at 60°)	110 - 130	%	ASTM D-523
Oxygen (T=23°C, RH=0%)	54 - 56	ml/m2.day	ASTM D-3985
Water Vapor (T=40°C, RH=90%)	150 - 170	g/m2.day	JIS Z-0208
Coefficient of Friction (Static)	0.84 - 0.88	—	ASTM D-1894
Coefficient of Friction (Dynamic)	0.84 - 0.88	—	ASTM D-1894
Tensile Strength at Yield	21 - 25	Mpa	ISO 527-3
Tensile Strength at Break	115 - 135	Mpa	ISO 527-3
Tensile Elongation at Break	495 - 515	%	ISO 527-3
Tensile Modulus	400 - 500	Mpa	ISO 527-3
Tear Load	2.2 - 2.4	N	ASTM D1922
Puncture Energy	33 - 35	mJ	JAS P-1019
Puncture Deformation	10.5 - 11.5	mm	JAS P-1019
Spencer Impact Energy	850 - 950	mJ	ASTM D3420
Flex Crack (Gelboflex) (at 23°C 1000 Cycles)	max. 5	Holes/0,04m2	Mil B-131C
Flex Crack (Gelboflex) (at 5°C 100 Cycles)	0	Holes/0,04m2	Mil B-131C
Thermoforming Depth	max. 100 - 120	mm	UBE METHOD
Relative Viscosity (96% H2SO4) (Measured on Base Polymer, Average Value)	4.05	—	—

Technical Details & Test Data

Notes

• Equipment: 5 layers airblown line.
• Die: Diameter = 90 mm • Gap = 1,4 mm.
• Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
• PA layer delaminated for the tests.
• Layer thickness distribution: PE = 50μm, PA = 50μm,
• PE = 50μm (Total film thickness = 150μm).
• Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
• Film orientation: Blow-up ratio = 2,1 •
• Take-off speed = 6m min-1.
• Samples conditioning and testing conditions: T = 23ºC, RH = 50%.

UBE Nylon Grades for Grass Timmer

Grades Types		Line strength	Knot strength	Flexibility	Heat resistance
Soft	UBE Nylon 6434 MT1	Exceptional	Exceptional	Exceptional	Suitable

UBE Nylon Grades for Fishing Lines

Grades Types		Line strength	Knot strength	Flexibility	Heat resistance
Soft	UBE Nylon 6434 MT1	Exceptional	Exceptional	Exceptional	Exceptional