Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
Durable with high toughness and fatigue resistance (PP retains its shape after torsion, bending, and/or flexing); low friction and smooth surfaces; semi-flexible; chemical-resistant to a wide range of bases and acids, including industrial cleaning agents; high electrical resistance; translucent; low density resulting in lightweight parts (high strength-to weight ratio); excellent layer bonding; adequate bed adhesion and low warping when using adhesion sheets
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Functional prototypes, living hinges, connectors, lab equipment, moldings, stationery folders, packaging, storage boxes, protective covers, and light shades
Non-suitable for Food contact and in vivo applications. Long term outdoor usage or applications where the printed part is exposed to temperatures higher than 105 °C.
Properties
- Color
- Physical Form
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Hardness (Rockwell, Durometer) | 45 | Shore D | — |
Tensile Modulus (1 mm/min) | 390 (220) | MPa | ISO 527 |
Tensile Stress at Yield (50 mm/min) | 14 (8.7) | MPa | ISO 527 |
Tensile Stress at Break (50 mm/min) | No break within | MPa | ISO 527 |
Elongation at Yield (50 mm/min) | 13 (18) | — | ISO 527 |
Elongation at Break (50 mm/min) | min. 200 (min. 300) | % | ISO 527 |
Flexural Strength | 14 (13) | MPa | ISO 178 |
Flexural Modulus | 350 (305) | MPa | ISO 178 |
Izod Impact Strength, Notched (23°C) | 27.1 | kJ/m2 | ISO 180 |
Charpy Impact Strength (23°C) | 10 | kJ/m2 | — |
Value | Units | Test Method / Conditions | |
Diameter | 2.85 ± 0.05 | mm | — |
Net Filament Weight | 500 | g | — |
Filament Length | ~ 88 | m | — |
Specific Gravity | 0.89 | — | ISO 1183 |
Haze (1Mmt) | 28 | % | ISO 14782 |
Gloss | 90 | % | ASTM D523 |
Value | Units | Test Method / Conditions | |
Melt Mass-Flow Rate (230°C, 2.16 kg) | 20 | g/10 min | ISO 1133 |
Vicat Softening Temperature (5N) | 115 | °C | ISO 306 |
Melting Temperature | 130 | °C | DSC |
Value | Units | Test Method / Conditions | |
Volume Resistivity | min. 10^16 | Ohm-cm | — |
Dissipation Factor (1 Mhz) | 0.003 | — | ASTM D150-11 |
Dielectric constant (1 MHz) | 1.91 | — | ASTM D150-11 |
Technical Details & Test Data
- Notes
Properties reported here are average of a typical batch. The 3D printed test specimens were printed in the XY plane, using the normal quality profile in Ultimaker Cura 2.1, an Ultimaker 2+, a 0.4 mm nozzle, 90% infill, 250 °C nozzle temperature, and 70 °C. The values are the average of five white and five black specimens for the tensile, flexural, and impact tests. The Shore hardness D was measured in a 7-mm-thick square printed using the normal quality profile in Utlimaker Cura 2.5, an Ultimaker 3, a 0.4 mm print core, and 100% infill. The electrical properties were measured on a 54-mm-diameter disk with 3 mm thickness printed in the XY plane, using the fine quality profile (0.1 mm layer height) in Ultimaker Cura 3.2.1, an Ultimaker 3, a 0.4 mm print core, and 100% infill.