- Materials Features
- Features
Exceptional wear and tear resistance, high impact strength, Shore A hardness of 95, up to 580% elongation at break, and good corrosion resistance to many common industrial oils and chemicals.
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Functional prototyping, grips, guides, hinges, sleeves, snap-fit parts, and protective cases
Non-suitable for Food contact and in vivo applications. Long term UV and/or moisture immersion and applications where the printed part is exposed to temperatures higher than 100 °C.
Properties
- Physical Form
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Hardness | 95 | Shore A | ASTM D2240 |
Tensile Modulus | 26 | MPa | ASTM D638 |
Tensile Stress at Yield | 8.6 | MPa | ASTM D638 |
Tensile Stress at Break | 39 | MPa | ASTM D638 |
Elongation at Yield | 55 | % | ASTM D638 |
Elongation at Break | 580 | % | ASTM D638 |
Flexural Strength | 4.3 | MPa | ISO 178 |
Flexural Modulus | 78.7 | MPa | ISO 178 |
Izod Impact Strength, Notched (23°C) | 34.4 | kJ/m2 | ISO 180 |
Abrasion Resistance (Mass Loss, 10,000 Cycles) | 0.06 | g | ASTM D4060 |
Value | Units | Test Method / Conditions | |
Diameter | 2.90 ± 0.13 | mm | Dual-axis laser gauge |
Max Roundness Deviation | 0.07 | mm | Dual-axis laser gauge |
Net Filament Weight | 750 | g | — |
Filament Length | ~ 96 | m | — |
Specific Gravity | 1.22 | — | ASTM D782 |
Flame Classification | HB Class | — | ICE 60695-11-10 |
Moisture Absorption (24H) | 0.18 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Melt Mass-Flow Rate (225°C, 1.2 kg) | 15.9 | g/10 min | ISO 1133 |
Heat Detection (0.455 Mpa) | 74 | °C | ASTM D648 |
Heat Deflection (1.82 Mpa) | 49 | °C | ASTM D648 |
Glass Transition | -24 | °C | DSC |
Coefficient of Thermal Expansion | 100·10-6 | °C-1 | ASTM E693 |
Melting Temperature | 220 | °C | DSC |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10^11 | Ohm-cm | IEC 60093 |
Surface Resistance | 2·1014 | Ω | IEC 60093 |
Dissipation Factor (1 Mhz) | 0.058 | — | ASTM D150-11 |
Dielectric constant (1 MHz) | 4.12 | — | ASTM D150-11 |
Technical Details & Test Data
- Notes
Properties reported here are average of a typical batch. The tensile test bars were printed with two shells, 107% material flow, nozzle temperature 260 °C, bed temperature 45 °C, nozzle diameter 0.8 mm, 40 mm/s infill speed, 30 mm/s print speed, and layer height 0.3 mm. The flexural and impact bars were printed in the XY plane, using the normal quality profile in Ultimaker Cura 2.1, an Ultimaker 2+, a 0.4 mm nozzle, 90% infill, 235 °C nozzle temperature, and 70 °C build plate temperature. The values are the average of five white and five black specimens for the flexural and impact test. The Shore hardness D was measured in a 7-mm-thick square printed in the XY plane, using the normal quality profile in Ultimaker Cura 2.5, an Ultimaker 3, a 0.4 mm print core and 100% infill. The electrical properties were measured on a 54-mm-diameter disk with 3 mm thickness printed in the XY plane, using the fine quality profile (0.1 mm layer height) in Ultimaker Cura 3.2.1, an Ultimaker 3, a 0.4 mm print core, and 100% infill.
- Color information
Color Color code TPU 95A White RAL 9010 TPU 95A Black RAL 9005 TPU 95A Red RAL 3031 TPU 95A Blue RAL 5002