Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
Excellent chemical resistance, temperature resistance, toughness, and dimensional stability. Good interlayer adhesion (especially when using the front enclosure add-on). Good bed adhesion (especially when using the adhesion sheets). And low levels of ultrafine particles (UFPs) and volatile organic compounds (VOCs). Allows printing of translucent parts with the transparent filament option
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Visual and functional prototyping, and short-run manufacturing
Non-suitable for Food contact and in vivo applications. Long term outdoor usage or applications where the printed part is exposed to temperatures higher than 100 °C.
Properties
- Physical Form
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Hardness (Rockwell, Durometer) | 75 | Shore D | — |
| Tensile Modulus (1 mm/min) | 1,575 (1,128.5) | MPa | ISO 527 |
| Tensile Stress at Yield (50 mm/min) | 43 (35.2) | MPa | ISO 527 |
| Tensile Stress at Break (50 mm/min) | 52 (33) | MPa | ISO 527 |
| Elongation at Yield (50 mm/min) | 0.07 (0.06) | — | ISO 527 |
| Elongation at Break (50 mm/min) | 2.1 (0.066) | — | ISO 527 |
| Flexural Strength | 64 (65) | MPa | ISO 178 |
| Flexural Modulus | 1,575 (1,555) | MPa | ISO 178 |
| Izod Impact Strength, Notched (23°C) | 860 (6.2) | J/m (kJ/m2) | ISO 180 |
| Value | Units | Test Method / Conditions | |
| Diameter | 2.85 ± 0.10 | mm | — |
| Max Roundness Deviation | 0.1 | mm | — |
| Net Filament Weight | 700 | g | — |
| Filament Length | ~ 93 | m | — |
| Specific Gravity | 1.18 | — | — |
| Value | Units | Test Method / Conditions | |
| Melt Mass-Flow Rate (240°C, 2.16 kg) | 8.5 | g/10 min | — |
| Heat Detection (0.455 Mpa) | 94 | °C | ASTM D648 |
| Heat Deflection (1.82 Mpa) | 81 | °C | ASTM D648 |
| Value | Units | Test Method / Conditions | |
| Dissipation Factor (1 Mhz) | 0.015 | — | ASTM D150-11 |
| Dielectric constant (1 MHz) | 2.77 | — | ASTM D150-11 |
Technical Details & Test Data
- Notes
Properties reported here are average of a typical batch. The 3D printed test specimens were printed in the XY plane, using the normal quality profile in Ultimaker Cura 2.1, an Ultimaker 2+, a 0.4 mm nozzle, 90% infill, 250 °C nozzle temperature, and 70 °C. The values are the average of five white and five black specimens for the tensile, flexural, and impact tests. The Shore hardness D was measured in a 7-mm-thick square printed using the normal quality profile in Utlimaker Cura 2.5, an Ultimaker 3, a 0.4 mm print core, and 100% infill. The electrical properties were measured on a 54-mm-diameter disk with 3 mm thickness printed in the XY plane, using the fine quality profile (0.1 mm layer height) in Ultimaker Cura 3.2.1, an Ultimaker 3, a 0.4 mm print core, and 100% infill.
- Color information
CPE+ Black RAL 9005 CPE+ White RAL 9010(est.)