Vectorply C-LT 2200

Identification & Functionality

Chemical Family

Carbon Fiber

Reinforcement Form

0/90 Fabric

Reinforcement Material

Carbon Fibers

Composite Materials Functions

Reinforcement

Architecture

0/90

Technologies

Composite Materials

Product Families

Composite Materials — Reinforcements

Carbon Fiber

Features & Benefits

Materials Features

Corrosion Resistant,

Cost Effective,

High Impact Resistance,

Light Weight

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Industrial

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Building & Construction — Infrastructure, Roads & Paving

Pavement, Highways, Roads & Bridges

Industrial — Military & Defense

Advanced Materials,

Body Armor

Industrial — Power, Water & Utilities

Renewable Energy

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Aerospace & Aviation,

Marine

Compatible Polymers & Resins

Polyesters,

Vinyl Esters

Composites End Use

Pipe Reinforcement,

Snowboards

Properties

Physical Form

Fabric

Dry Thickness

0.040 (1.02)

Total Weight

22.96 (779)

Roll Width

50 (1270)

Roll Weight

116 (53)

Roll Length

58 (53)

Technical Details & Test Data

Fiber Architecture Data

• 0 ° : 11.48 oz/sq.yd / 389 g/sq.m
• 45 ° : n/a
• 90 ° : 11.48 oz/sq.yd / 389 g/sq.m
• -45 ° : n/a
• Chopped Mat : n/a

Laminated Properties

Laminate Weight

	C-LT 2200 Resin Infused	C-LT 2200 Open Mold
Fiber	0.78 kg/sq.m	0.78 kg/sq.m
Resin	0.44 kg/sq.m	0.95 kg/sq.m
Total	1.22 kg/sq.m	1.73 kg/sq.m

Physical Properties

	C-LT 2200 Resin Infused	C-LT 2200 Open Mold
Density	1.53 g/cc	1.41 g/cc
fiber Content	54% by Vol.	35% by Vol.
Thickness	0.8 mm	1.2 mm

Laminate Modulii

	C-LT 2200 Resin Infused	C-LT 2200 Open Mold
Ex	61.86 GPa	41.80 GPa
Ey	61.86 GPa	41.80 GPa
Gxy	4.09 GPa	2.91 GPa
Ex,flex.	58.77 GPa	39.71 GPa
Ey,flex.	58.77 GPa	39.71 GPa

Ultimate Stress

	C-LT 2200 Resin Infused	C-LT 2200 Open Mold
Long. Ten.	681.5 MPa	460.5 MPa
Long. Comp.	483.4 MPa	326.7 MPa
Trans. Ten.	681.5 MPa	460.5 MPa
Trans. Comp.	483.4 MPa	326.7 MPa
In-Plane Shear	81.8 MPa	58.2 MPa
Long. Flex.	429.3 MPa	290.1 MPa
Trans. Flex.	429.3 MPa	290.1 MPa

In-Plane Stiffness, "EA" 

	C-LT 0900 Resin Infused	C-LT 0900 Open Mold
(EA)x	49,338 N/mm	51,232 N/mm
(EA)x	49,338 N/mm	51,232 N/mm
(GA)xy	3,264 N/mm	3,565 N/mm

Ultimate In-Plane Load

	C-LT 2200 Resin Infused	C-LT 2200 Open Mold
Long. Ten.	544 N/mm	564 N/mm
Long. Comp.	386 N/mm	400 N/mm
Trans. Ten.	544 N/mm	564 N/mm
Trans. Comp.	386 N/mm	400 N/mm
In-Plane Shear	65 N/mm	71 N/mm

Packaging & Availability

Packaging Type

Bags,

Boxes