Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Form
- Reinforcement Material
- Composite Materials Functions
- Architecture
- 0/45/90/-45 Quadraxial
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Composites End Use
Properties
- Physical Form
- Dry Thickness
- 0.035 (0.89)
- Total Weight
- 18.19 (617)
- Roll Width
- 50 (1270)
- Roll Weight
- 113 (51)
- Roll Length
- 71 (65)
Technical Details & Test Data
- Fiber Architecture Data
- 0 ° : 4.64 oz/sq.yd / 157 g/sq.m
- 45 ° : 4.46 oz/sq.yd / 151 g/sq.m
- 90 ° : 4.64 oz/sq.yd / 157 g/sq.m
- -45 ° : 4.46 oz/sq.yd / 151 g/sq.m
- Chopped Mat : n/a
- Laminated Properties
Laminate Weight
C-QX 1800
Resin InfusedC-QX 1800
Open MoldFiber
Resin
Total0.62 kg/sq.m
0.35 kg/sq.m
0.96 kg/sq.m0.62 kg/sq.m
0.75 kg/sq.m
1.37 kg/sq.mPhysical Properties
C-QX 1800
Resin InfusedC-QX 1800
Open MoldDensity
Fiber Content
Thickness1.53 g/cc
54% by Vol.
0.6 mm1.41 g/cc
35% by Vol.
1.0 mmLaminate Modulii
C-QX 1800
Resin InfusedC-QX 1800
Open MoldEx
Ey
Gxy
Ex,flex.
Ey,flex.43.28 GPa
43.28 GPa
16.32 GPa
41.12 GPa
41.12 GPa29.35 GPa
29.35 GPa
11.02 GPa
27.88 GPa
27.88 GPaUltimate Stress
C-QX 1800
Resin InfusedC-QX 1800
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear
Long. Flex.
Trans. Flex.519.4 MPa
331.8 MPa
519.4 MPa
331.8 MPa
250.2 MPa
315.3 MPa
315.3 MPa352.2 MPa
225.0 MPa
352.2 MPa
225.0 MPa
169.0 MPa
213.8 MPa
213.8 MPaIn-Plane Stiffness, "EA"
C-QX 1800
Resin InfusedC-QX 1800
Open Mold(EA)x
(EA)y
(GA)xy27,347 N/mm
27,347 N/mm
10,311 N/mm28,495 N/mm
28,495 N/mm
10,699 N/mmUltimate In-Plane Load
C-QX 1800
Resin InfusedC-QX 1800
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear328 N/mm
210 N/mm
328 N/mm
210 N/mm
158 N/mm342 N/mm
218 N/mm
342 N/mm
218 N/mm
164 N/mm