Knowde Enhanced TDS
Identification & Functionality
- Cleaning Ingredients Functions
- Fluids & Lubricants Functions
- Industrial Additives Functions
Features & Benefits
- Fluids & Lubricants Features
- HII Features
Applications & Uses
- Applications
- Fluids & Lubricants Type
- Fluids & Lubricants End Use
- Home Care Applications
- I&I Cleaning Applications
- Use Level
- 0.1 – 0.5%
- Recommended Applications
It is recommended in the applications of synthetic coolants and cutting fluids, Industrial cooling towers, water based lubricants, alkaline metal cleaners, aerosol formulations, low foam alkaline cleaners, radiator fluid additive, treating baths for copper and copper alloys, water based paints and coatings.
Properties
- Physical Form
- Appearance
- Clear amber viscous liquid
- Dispersible in
- Oils
- Insoluble in
- solvents
- Typical Properties
- Typical Properties
It is a corrosion inhibitor for metal in aqueous systems at pH >= 7. It is biodegradable, non-phenolic, nitrite free. It is stable in hard water, unstable in acid systems and virtually non-foaming. It is effective at low use levels (0.1 – 0.5%).
Value | Units | Test Method / Conditions | |
Activity | min. 95 | % | — |
Color | max. 12 | Gardner | — |
Density (25°C) | 1.02 | g/cc | — |
pH Value (1% in Distilled Water) | 7.0 - 8.0 | — | — |
Solids Content | min. 95 | % | — |
Technical Details & Test Data
- Product Efficacy Studies
Metal Panel Submersion Corrosion Testing using DeCORE APCI-95MOD:
The bottom halves of the metal panels were submerged into a solution containing 0.25% & 1.0% by weight DeCORE APCI-95MOD in hard water (100 ppm as CaCO3& 71 ppm as chloride) at room temperature. The top half of the panel was exposed to the vapor phase in closed glass containers.Photos taken after 120 days of testing.Metal Panel Submersion Corrosion Testing using DeCORE APCI-95MOD:
The bottom halves of the metal panels were submerged into a solution containing 0.25% & 1.0% by weight DeCORE APCI-95MOD in hard water (100 ppm as CaCO3& 71 ppm as chloride) at room temperature. The top half of the panel was exposed to the vapor phase in closed glass containers.Photos taken after one year of testing.