Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
Features & Benefits
- Materials Features
- Features
- The largest range of transparent colors on the market.
- The TRANSPARENT range ranges from very striking red, yellow, blue and green colors, to very dark almost opaque colors with a blackish appearance, passing through gray, blue and brown smoky colors.
- High optical quality, without distortion and transparent.
- Colors with the highest brightness on the market and maximum resistance to aging. Color intensity is maintained in all thicknesses.
- It is easily machined.
- It can be polished obtaining a total shine.
- It allows to be slightly cold bent.
- It can be thermoformed.
- Lighter than glass.
- Impact resistence.
- Low thermal conductivity.
Applications & Uses
- Markets
- Applications
- Composites End Use
- Plastics & Elastomers End Uses
- Applications
- Decoration pieces (gift, florist, hospitality, etc.)
- Nautical vessel windows.
- Protections of industrial machinery.
- Lettering.
- Railings, partitions and partitions.
- Furniture.
- Displays for food in restaurants and bars.
- Signaling and signage.
- Skylights.
- Advertising posters.
- Enclosures.
- Lettering.
Properties
- Color
- Physical Form
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Optical Properties
- Optical Properties
Light transmission Value Standard a) Total luminous transmission of light at 380-780 nm Depends on color%
ISO2857
b) Light transmission at 420 nm c) Light transmission at 420 nm after 1000 hours in the xenon
| Value | Units | Test Method / Conditions | |
| Density | 1.2 | g / cm3 | ISO 1183 |
| Water Absorption | 0.3 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Elongation at Elastic Limit (at Break) | 5.0 | % | ISO 527 |
| Flexural Srength | 100.0 | MPa | ISO 178 |
| Impact Resistance (Charpy Method) | 17.0 | kJ / m-2 | ISO 179 / 2D |
| Modulus of Elasticity in Tension (Test 1, Speed B) | 3000.0 | MPa | ISO 527 |
| Rockwell Hardness | 100.0 | — | ISO 2039-2 |
| Tensile Srength (Test 1, Speed B) | 72.0 | MPa | ISO 527 |
| Value | Units | Test Method / Conditions | |
| Bending Temperature under Load (Method A, 1.8MPa) | 105.0 | °C | — |
| Coefficient of Linear Expansion | 70.6 x 10^-6 | K-1 | — |
| Dimensional Variation at Elevated Temperature (Shrinkage) | 23.0 | % | — |
| VICAT Softening Temperature | 105-120 | °C | — |
| Value | Units | Test Method / Conditions | |
| Dielectric Constant (1Megahertz) | 2.8 | — | DIN53483 |
| Dielectric Constant (50 Hz) | 3.6 | — | DIN53483 |
| Specific Resistance | min. 10^15 | Ohm | DIN53458 |
| Volume Resistance | min. 10^15 | Ohm cm | DIN53458 |
| Value | Units | Test Method / Conditions | |
| Refractive Index No. (Method A) | 1492.0 | — | ISO / R 489 |
Packaging & Availability
- Formats
- Size:
- They are manufactured with the European standard of 3050 x 2050 mm.
- They can be supplied cut to size.
- Thicknesses:
- The standard is 3mm.
- It can be manufactured in any thickness upon request.
- It should be taken into account that for thicknesses greater than 10 mm the color intensity of the edge is noticeably reduced. If requested, you can ask to increase the intensity of the color, taking into account that it will also increase the intensity of the color on the surface of the plate.
- Size: