- Excellent Coefficient of Friction - Nylube contains a combined liquid/solid lubricant system which allows for a coefficient of friction as low as 0.08. A figure which is below that of almost any other polymer available at present. Nylube has substantially improved the wear resistance abilities compared to that of any other currently available lubricated grade of cast nylon, whilst retaining excellent physical property characteristics
Applications & Uses
- Markets
- Applications
Properties
- Color
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
- Flammability
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (Sample Type 1B, 50mm/min) | 80 - 90 | MPa | ISO 527-1/2;1993 |
| E-modulus (Sample Type 1B, 50mm/min) | 3600 - 4000 | MPa | ISO 527-1/2:1993 |
| Elongation at Break (Sample Type 1B, 50mm/min) | min. 30 | % | ISO 527-1/2:1993 |
| Compressive Strength (Sample Type B, 5mm/min) | 105 - 125 | MPa | ISO 604:2002 |
| Compressive Modulus (Sample Type A, 1mm/min) | 2500 - 2700 | MPa | ISO 604:2002 |
| Flexural Strength (1.5mm/min) | 115 - 125 | MPa | ISO 178:2001 |
| Flexural Modulus (1.5mm/min) | 3350 - 3600 | MPa | ISO 178:2001 |
| Izod Impact Strength (Sample Type A, notched) | 5.5 - 7.0 | kJ/mm² | ISO 180:2000 |
| Dynamic Coefficient of Friction (31.4m/min, 1.75MPa) | 0.075 | - | - |
| Limiting PV | 100.0 | MPa/m | - |
| K-Factor (Wear Factor, 31.4m/min, 1.75MPa) | 3.9x10⁻⁶ | mm³/Nm | - |
| Hardness | 83.0 | Shore D | ISO 868:2003 |
| Value | Units | Test Method / Conditions | |
| Density (Test Method A) | 1.141 | g/cm³ | ISO 1183:1997 |
| Moisture Absorption (Equilibrium, 50% RH, 23°C) | 2.0 | % | ISO 62:1999(modified) |
| Water Absorption (24 hrs, Immersion at 23°C) | 0.2 | % | ISO 62:1999 (modified) |
| Water Absorption (24 hrs Saturation, Immersion at 23°C) | 5.9 | % | ISO 62:1999 |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (Tg) | 222.0 | °C | - |
| Glass Transition Temperature | 65.0 | °C | ISO 11359:1999 |
| Heat Deflection Temperature (HDT/A, 1.80MPa) | 75.0 | °C | ISO 75 |
| Maximum/Minimum Continuous Service Temperatures | 110/-40 | °C | - |
| Maximum/Minimum Intermittent Service Temperatures | 180/-100 | °C | - |
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 8x10⁻⁵ | °C⁻¹ | ISO 11359-2:1999 |
| Thermal Conductivity (Mean T = 20°C) | 0.25 | W/m°C | ISO 8301:1991 |
| Value | Units | Test Method / Conditions | |
| Dielectric Constant (1 Hz) | 3.7 | - | IEC 60250:1969-01 |
| Dielectric Constant (100 Hz) | 4.0 | - | IEC 60250:1969-01 |
| Dissipation Factor (100 Hz) | 0.013 | - | IEC 60250:1969-01 |
| Dielectric Strength | 25.0 | kV/m | IEC 60243:-1:1998-01 |
| Volume Resistivity | min. 1x10¹³ | ohm.m | IEC 60093:1980-01 |
| Surface Resistivity | min. 1x10¹² | ohm.m | IEC 60093:1980-01 |
| Comparative Tracking Index | 600.0 | CTI | IEC 60112:2003-01 |
| Value | Units | Test Method / Conditions | |
| Flammability | HB | - | IEC 60695-11-10:2003-08 |
Regulatory & Compliance
- Certifications & Compliance
- FDA Compliant
Much like Nylacats Oilon, Nylacast Nylube is suitable for use in applications in the food and pharmaceutical industries as a result of the premium FDA compliant lubricate throughout the material.
Packaging & Availability
- Availability
Rod 10mm-500mm DIA Tube 50mm-1000mm OD Plate 6mm-100mm THICKNESS Cut to size Available upon request