- Oil Lubrication System - Premium Oil-based lubricant is uniformly distributed throughout the Nylacast Oilon material product to guarantee constant whole life performance, The lubricant will not drain, machine, spin, leech or dry out and never needs replenishment.
Applications & Uses
- Markets
- Applications
Properties
- Color
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
- Flammability
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (Sample Type 1B, 50mm/min) | 74 - 78 | MPa | ISO 527-1/2;1993 |
| E-modulus (Sample Type 1B, 50mm/min) | 3500 - 3700 | MPa | ISO 527-1/2:1993 |
| Elongation at Break (Sample Type 1B, 50mm/min) | max. 30 | % | ISO 527-1/2:1993 |
| Compressive Strength (Sample Type B, 5mm/min) | 110 - 20 | MPa | ISO 604:2002 |
| Compressive Modulus (Sample Type A, 1mm/min) | 2100 - 2500 | MPa | ISO 604:2002 |
| Flexural Strength (1.5mm/min) | 105 - 125 | MPa | ISO 178:2001 |
| Flexural Modulus (1.5mm/min) | 3300 - 3600 | MPa | ISO 178:2001 |
| Izod Impact Strength (Sample Type A, notched) | 5.0 - 6.5 | kJ/mm² | ISO 180:2000 |
| Dynamic Coefficient of Friction (31.4m/min, 1.75MPa) | 0.089 | — | — |
| Limiting PV | 100.0 | MPa/m | — |
| K-Factor (Wear Factor, 31.4m/min, 1.75MPa) | 2.2x10⁻⁵ | mm³/Nm | — |
| Hardness | 82.0 | Shore D | ISO 868:2003 |
| Value | Units | Test Method / Conditions | |
| Density (Test Method A) | 1.138 | g/cm³ | ISO 1183:1997 |
| Moisture Absorption (Equilibrium, 50% RH, 23°C) | 2.0 | % | ISO 62:1999(modified) |
| Water Absorption (24 hrs, Immersion at 23°C) | 0.2 | % | ISO 62:1999 (modified) |
| Water Absorption (24 hrs Saturation, Immersion at 23°C) | 6.1 | % | ISO 62:1999 |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (Tg) | 222.0 | °C | — |
| Glass Transition Temperature | 65.0 | °C | ISO 11359:1999 |
| Heat Deflection Temperature (HDT/A, 1.80MPa) | 75.0 | °C | ISO 75 |
| Maximum/Minimum Continuous Service Temperatures | 110/-40 | °C | — |
| Maximum/Minimum Intermittent Service Temperatures | 170/-100 | °C | — |
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 8x10⁻⁵ | °C⁻¹ | ISO 11359-2:1999 |
| Thermal Conductivity (Mean T = 20°C) | 0.25 | W/m°C | ISO 8301:1991 |
| Value | Units | Test Method / Conditions | |
| Dielectric Constant (1 Hz) | 3.7 | — | IEC 60250:1969-01 |
| Dielectric Constant (100 Hz) | 4.0 | — | IEC 60250:1969-01 |
| Dissipation Factor (100 Hz) | 0.014 | — | IEC 60250:1969-01 |
| Dielectric Strength | 25.0 | kV/m | IEC 60243:-1:1998-01 |
| Volume Resistivity | min. 1x10¹³ | ohm.m | IEC 60093:1980-01 |
| Surface Resistivity | min. 1x10¹² | ohm.m | IEC 60093:1980-01 |
| Comparative Tracking Index | 600.0 | CTI | IEC 60112:2003-01 |
| Value | Units | Test Method / Conditions | |
| Flammability | HB | — | IEC 60695-11-10:2003-08 |
Regulatory & Compliance
- Certifications & Compliance
- FDA Compliant
FDA compliant medical white oil is used within Nylacast Oilon rather than silicone fluids.
Packaging & Availability
- Availability
Rod 10mm-500mm DIA Tube 50mm-1000mm OD Plate 6mm-100mm THICKNESS Cut to size Available upon request