Ecolon® MRGF1878-BKJA6A

30% Mineral/Glass-Reinforced Nylon Resin (PA6), Ford Color Match

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber, Mineral

Flexural Modulus: 7790.0 - 7790.0 MPa

Knowde Enhanced TDS

Identification & Functionality

Applications & Uses

Markets: Automotive & Transportation
Applications: Automotive & Transportation — Automotive
Exterior & Body,
Interior,
Other Automotive Applications
Plastics & Elastomers End Uses: Automotive Applications,
Automotive Exterior Parts,
Automotive Interior Parts
Plastics & Elastomers Processing Methods: Injection Molding

Properties

	Value	Units	Test Method / Conditions
Tensile Strength	105	MPa	ISO 527
Tensile Elongation	2.0	%	ISO 527
Flexural Modulus	11.3	psi(105)	ISO 178
Flexural Strength	23200	psi	ASTM D790
Charpy Notched Impact Strength	0.82	ft-lbs/in	ISO 180
Izod notched impact strength, +23°	5	kJ/m2	ISO 180/1A

	Value	Units	Test Method / Conditions
Molding Shrinkage - Flow	0.3 - 0.7	%	ISO DIS 294
Molding Shrinkage - Transverse	0.6 - 1.0	%	ISO DIS 294
Density	1380	kg/m3	ASTM D 792

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (264 psi)	390	°F	ISO 75
Temperature of deflection under load (1.80 Mpa)	200	°C	ISO 75-1/-2
Melting temperature (10°C/min)	220	°C	ISO 11357-1/-3
Melting Point	430	°F	ISO 3146

	Value	Units	Test Method / Conditions
Filler Content	30	%	ISO 3451