- Broad hardness range: Shore 00 to D 90
- Adjustable flow properties
- Filled and unfilled systems
- Good temperature cycle behavior
- Clear, UV-resistant systems
- Low dielectric constant
- Self-extinguishing systems in accordance with UL 94 V-0
- Good adhesion not only on conventional thermoplastics, but also on high-performance plastics such as LCP, BMC, etc.
- Operating temperature range: -60 °C to +165 °C
- Pot life adjustable from 1 to 90 minutes
- Thermal conductivity up to 2.0 W/m·K
Applications & Uses
Properties
- Typical Properties
- Flammability
| Value | Units | Test Method / Conditions | |
| Density of Hardener at 22 °C | 1.20 –1.24 | g/cm³ | DIN EN ISO 2811-1:2016-08 |
| E modulus | 15 | N/mm² | DIN EN ISO 527-2:2012-06 |
| Volume Resistivity | 10^14 | Ω·cm | DIN EN 62631-3-1:2017-01 |
| Thermal Conductivity | 0.2 | W/m·K | DIN EN ISO 22007-2:2015-12 |
| Coefficient of Expansion (<–60 °C) | 56 | ppm/K | TMA ISO 11359-2:1999-10 |
| Coefficient of Expansion (>–60 °C) | 211 | ppm/K | — |
| Density of Resin at 22 °C | 0.91 – 0.93 | g/cm³ | DIN EN ISO 2811-1:2016-08 |
| Dielectric Constant ε (at 50 Hz, 23 °C) | 3.1 | — | DIN EN IEC 62631-2-1:2018-12 |
| Dielectric Strength | 25 | kV/mm | DIN EN 60243-1:2014-01 |
| Glass Transition Temperature | –60 | °C | TMA ISO 11359-2:1999-10 |
| Loss Factor tan δ (at 50 Hz, 23 °C) | 0.014 | — | DIN EN IEC 62631-2-1:2018-12 |
| Mixed Viscosity at 22 °C | 1200 –1600 | mPa·s | Rotational viscometer |
| Mixing Ratio | 100 : 34 | Parts by Weight | — |
| Operating Temperature | –60 up to +120 | °C | — |
| Reactivity at 22 °C | 10 – 40 | min | — |
| Water Absorption | 0.2 | % | 30 days, 22 °C |
| Hardness | 60-75 | Shore A (D) | DIN ISO 7619-1:2012-02 |
| Hardness | 60 –75 | Shore A | DIN ISO 7619-1:2012-02 |
| Value | Units | Test Method / Conditions | |
| Flammability | HB | — | UL 94 |