Knowde Enhanced TDS
Identification & Functionality
- CI Name
- CI Number
- Chemical Family
- Chemical Name
- Pigment Type
- Plastics & Elastomers Functions
- H.S Code
- 28230000.0
- CAS No.
- 13463-67-7
- EC No.
- 236-675-5
- Technologies
- Product Families
- Chemical Formula
TiO2
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Application
FA-101 Anatase grade general purpose properties
1.Great stability:
The mature production technology and effective management contributes to the stability of FA-101 anatase grade general purpose titanium dioxide and it helps our customers produce more perfect products, too.
2.Excellent dispersibility:
The excellent dispersibility gives FA-101 anatase grade general purpose titanium dioxide a better performance, which gives rise to a better product of our customers.
3.Low oil absorption:
This feature reduces the loss of materials effectively, so do our customers’ cost.
4.Strong hiding power:
Using much less material than similar products but can achieve a better hiding effect. Again, this feature also lowers our customers’ cost.
5.Good distribution of particle size and density:
This feature could prevent our customers’ products from getting hardened.
Properties
- Color
- Specifications
| Value | Units | Test Method / Conditions | |
| Mass Fraction of Tio2 | min. 98 | — | — |
| Mass Fraction of Volatiles (105°C) | max. 0.5 | — | — |
| Mass Fraction of Water Soluble | max. 0.6 | % | — |
| Mass Fraction of Screenings（45Ūm） | max. 0.1 | % | — |
| Color (Compared With Sample) | Unconfirmed | — | — |
| Relative Tint Scattering Strength (Compared With Sample) | Unconfirmed | % | — |
| Color of Powder L* | min. 98.2 | % | — |
| Color of Powder A* | max. 0.1 | — | — |
| Color of Powder B* | max. 1.2 | — | — |
| Tint Reducing Power (Compared With Sample) | min. 105 | — | — |
| Ph Value of Aqueous Suspension | 6.5~8.5 | — | — |
| Oil Absorption | Unconfirmed | g/100g | — |
| Water Dispensability | min. 85 | % | — |
| Molecular Weight | 79.9 | — | — |