| Value | Units | Test Method / Conditions | |
| Density (Dam) | 1.45 | g/cm3 | ISO 1183 |
| Post Shrinkage (Parallel, Dam) | 0.35 | % | Sim.ISO 294-4 |
| Post Shrinkage (Normal, Dam) | 0.45 | % | Sim.ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (at 1 mm/min, Dam) | 8000 | MPa | ISO 527 |
| Tensile Strength (at Break, 5 mm/min, Dam) | 115 | MPa | ISO 527 |
| Tensile Elongation (at Break, 5 mm/min, Dam) | 6 | % | ISO 527 |
| Flexural Modulus (at 2 mm/min, Dam) | 7000 | MPa | ISO 178 |
| Flexural Stress (at 3.5% Strain, 2 mm/min, Dam) | 145 | MPa | ISO 178 |
| Notched Izod Impact Strength (at 23°C, 50% RH, Dam) | 31 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at 23°C, 50% RH, Dam) | 93 | kJ/m2 | ISO 180 |
| Notched Izod Impact Strength (at -30°C, Dam) | 21 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at -30°C, Dam) | 81 | kJ/m2 | ISO 180 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 8 MPa, 120°C/h, Dam) | 105 | °C | ISO 75 |
| Vicat Softening Temperature (at 50 N, 120°C/h, Dam) | 160 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80 - 100 | °C | Desiccant Dryer |
| Drying Time | 6 - 8 | hrs | Desiccant Dryer |
| Mould Temperature | 35 | °C | — |
| Melt Temperature | 240 - 255 | °C | — |
Safety & Health
- Processing Note
Under the recommended processing condition small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.