Flame-retardant
Z-PEI 9085 has a V-0 flammability rating which means it can be safely used in aircraft interiors. Very low FST (Flame, Smoke, Toxicity) means the 3D printed components cause no harm in emergency scenarios.
- Aerospace-grade
Z-PEI 9085 has much higher thermal shock resistance than aluminum 6061 while having comparable strength-to-weight ratio.
- Heat-resistant
The material's heat resistance is equal to aluminum 6061 which means Z-PEI 9085 retains its mechanical properties in up to 167 °C.
-
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Industrial parts and tools,
- Aerospace interiors,
- Ductwork,
- Flameretardant components.
Properties
- Flame Rating
- Physical Form
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 54 | MPa | ISO 527 |
Tensile Modulus | 2050 | MPa | ISO 527 |
Tensile Elongation | 3 | % | ISO 527 |
Flexural Strength | 90 | MPa | ISO 178 |
Flexural Modulus | 2170 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Glass Transition Temperature | 186 | °C | DSC |
Deflection Temperature at 0.45 MPa (66psi) | 158 | °C | ISO 75 |
Value | Units | Test Method / Conditions | |
Density | 1.34 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Flamability Rating (1.5mm) | 0 | — | UL 94 |