Addilene® PMD 50312

Identification & Functionality

Additives Included

Impact Modifier

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene Copolymer

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Impact Modified

Applications & Uses

Markets

Automotive & Transportation

Applications

Automotive & Transportation — Automotive

Interior

Automotive & Transportation — Other Automotive & Transportation Applications

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Instrument Panel,

Automotive Interior Parts,

Consoles,

Door Panel,

Instrument Panel

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength	16	MPa	ISO 527
Charpy Notched Impact Strength (at 23°C)	64	kJ/m2	ISO 179-1/1eA
Hardness	60	Shore D	ISO 868
Hardness	60	Shore D	ASTM D 2240
Charpy Unnotched Impact Strength (at 23°C)	NB	kJ/m2	ISO 179-1/1eU
Yield stress	17	MPa	ISO 527
Strain at break	500	%	ISO 527
Elongation at Break	500	%	ISO 527-2/1A
Flexural modulus, 23°	800	MPa	ISO 178
Flexural Modulus	800	MPa	ISO 178
Izod Notched Impact Strength	NB	kJ/m2	ISO 180/1A
Charpy impact strength (+23°)	N	kJ/m2	ISO 179/1eU
Charpy notched impact strength (+23°)	64	kJ/m2	ISO 179/1eA
Stress at Break	16	MPa	ISO 527-2/1A
Stress at Yield Point	17	MPa	ISO 527-2/1A

Physical Properties

	Value	Units	Test Method / Conditions
Melt Volume Flow Rate - MVR (230°C/2.16 kg)	7	cm3/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Temperature of deflection under load (1.80 Mpa)	45	°C	ISO 75-1/-2
Melting temperature (10°C/min)	167	°C	ISO 11357-1/-3
Heat Deflection Temperature	45	°C	ISO 75-2/Af
Melting Point	165/168	°C	ISO 11357-3
Vicat Softening Point	135	°C	ISO 306/A50
Vicat softening temperature	135	°C	ISO 306

Electrical Properties

	Value	Units	Test Method / Conditions
CTI	min. 600	V	CEI 60112

Physico-Chemical Properties

	Value	Units	Test Method / Conditions
Density	0.9	g/cm3	ISO 1183-1
MVI (at 230°C-2.16Kg)	7	cm3/10min	ISO 1133-1

Fire Resistance

	Value	Units	Test Method / Conditions
Falling Ball Test	96	°C	CEI 60695-10-2

Technical Details & Test Data

Note

• The LOI measures are obtained through standard specimens of type I, with ignition of type A.
• The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.