| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (cond) | 15 | kJ/m2 | ISO 179-1/1eA |
| Hardness (Cond) | 71 | Shore D | ISO 868 |
| Charpy Notched Impact Strength (dam) | 5 | kJ/m2 | ISO 179-1/1eA |
| Hardness (Dam) | 82 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (cond) | NB | kJ/m2 | ISO 179-1/1eU |
| Charpy Unnotched Impact Strength (dam) | NB | kJ/m2 | ISO 179-1/1eU |
| Elongation at Break (cond) | min. 50 | % | ISO 527-2/1A |
| Elongation at Break (dam) | 30 | % | ISO 527-2/1A |
| Flexural Modulus (cond) | 900 | MPa | ISO 178 |
| Flexural Modulus (dam) | 2800 | MPa | ISO 178 |
| Izod Notched Impact Strength (cond) | 16 | kJ/m2 | ISO 180/1A |
| Izod Notched Impact Strength (dam) | 5.5 | kJ/m2 | ISO 180/1A |
| Stress at Break (cond) | 30 | MPa | ISO 527-2/1A |
| Stress at Break (dam) | 80 | MPa | ISO 527-2/1A |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature | 65 | °C | ISO 75-2/Af |
| Heat Deflection Temperature | 165 | °C | ISO 75-2/Be |
| Melting Point | 220 | °C | ISO 11357-3 |
| Value | Units | Test Method / Conditions | |
| CTI | min. 600 | V | CEI 60112 |
| Value | Units | Test Method / Conditions | |
| Density | 1.14 | g/cm3 | ISO 1183-1 |
| Value | Units | Test Method / Conditions | |
| Incandescent Glow Wire Flammability Test (2mm) | 750 | °C | CEI 60695-2-12 |
Technical Details & Test Data
- Note
- The values indicated above have been realized with standard specimens in room temperature, except if particular conditions:
- dam: specimens 48h after molding
- cond: specimens conditioned according to ISO 291 et ISO 1110. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties. The information given herein is the outcome of our research and experience. It is given in all good faith but can neither be interpreted as a warranty given by us nor incur our liability especially in the event of infringement of third party rights.