Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- Distinguishing Features
BECKOPOX™ EP 122w is much lower in viscosity than BECKOPOX™ EP 147w, shows slower drying and is easier water-emulsifiable. BECKOPOX™ EP 122w is preferably used for mineral substrates.
Applications & Uses
- Applications
- Application Method
- Compatible Substrates & Surfaces
- Coating Type
- Special Properties and Uses
Non-crystallizing liquid resin, low-viscous. Water reducible primers/coatings on mineral substrates, adhesives and water-washable jointing compounds for tiles, hydraulic epoxy mortars (ECC).
- Suggested Uses and Processing Information
BECKOPOX™ EP 122w is a low viscous, water-emulsifiable epoxy resin. In combination with water-thinnable or water-emulsifiable hardeners it is used to formulate coatings for concrete, jointing compounds and tile-adhesives.
The preferred reaction partner for concrete-coatings is BECKOPOX™ EH 623w (primers and topcoats can be formulated). For water-washable jointing compounds the best results are obtained with BECKOPOX™ EH 661 or EH 663. For coatings, BECKOPOX™ EP 122w is mixed 1 : 1 with BECKOPOX™ EH 623w or EH 659w in a dissolver, the mixture can be then emulsified with water under continuous stirring to the desired concentration.
These coating materials can be applied by brush, roller or spray gun. After 18-24 hours drying the next layer can be applied. Fully curing and mechanical resistance can be achieved within 8-10 days. To accelerate drying and the development of hardness, BECKOPOX™ EP 122w can be combined with BECKOPOX™ EP 384w.
Pigmentation
Pigmentation is carried out normally on a triple roll mill or perl mill. The compatibility of pigments has to be checked in advance. Preferred are inert pigments, like titanium dioxide, chromium oxide or iron oxide. After homogenous mixing of pigment-millbase and hardener, the formulation can be diluted with water. Processing time depends on the choice of hardener. The end of the processing time is not visible through viscosity increase or gelation.
Jointing compounds
For producing of jointing compounds BECKOPOX™ EP 122w is combined with BECKOPOX™ EH 661 or EH 663. Extenders are quartz powder or -sand. After application polluted tiles can be washed with water within the processing time of the compound.
MIXING RATIO AND POT LIFE
A blend of 100 g BECKOPOX™ EP 122w, 100 g BECKOPOX™ EH 659w/50WA, 100 g deionized water has a pot life at 23°C of approx. 3 - 4 hours, which can not be observed through a pronounced increase in viscosity, so that it should be used within this time period. The substrate temperature should not be below 10°C and the relative humidity not above 80%.
Properties
- Physical Form
- Emulsifiable in
- Water
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Iodine Color Number | max. 5 | % | — |
| Flash Point (Pensky-Martens) | min. 100 | °C | — |
| Density (20°C) | approx. 1.11 | g/cm³ | — |
| Epoxy Equivalent (Form of Delivery) | 190 - 200 | g/mol | — |
| Dynamic Viscosity (500 s⁻¹, 23°C) | 700 - 900 | mPa.s | — |
| Dynamic Viscosity (500 s⁻¹, 25°C) | 600 - 750 | mPa.s | — |
Storage & Handling
- Shelf Life
- 1 Year
- Storage and Handling
At temperatures up to 25°C storage stability packed in original containers amounts to at least 365 days.
When handling and processing epoxy resins and hardeners, the rules and regulations established by local authorities should be observed. A Material Safety Data Sheet is available on request.