Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
Applications & Uses
- Cure Method
Properties
- Physical Form
- Component A
- Component B
- Cured Properties
Value | Units | Test Method / Conditions | |
Viscosity | 1500000 | cps | — |
Value | Units | Test Method / Conditions | |
Viscosity | 1500000 | cps | — |
Value | Units | Test Method / Conditions | |
Working Time (at 75°F/ 24°C) | 3 - 5 | minutes | — |
Fixture Time (at 75°F/ 24°C) | 20 - 30 | minutes | — |
Full Cure (at Room Temperature, For Full Properties) | 24 | hours | — |
Operating Temperature | -40 to 266 (-40 to 130) | °F (°C) | — |
Density (at Room Temperature, Mixed) | 9.5 (1.15) | lbs/gal (g/cc) | — |
Flash Point (at Room Temperature) | min. 392 (min. 200) | °F (°C) | — |
Mix Ratio (Part A:Part B) | 1:1 | — | — |
Hardness (at Room Temperature) | 80 | — | Shore D |
Lap Shear Strength (at Room Temperature, AL to AL) | min. 2,900 | psi | — |
Tensile Strength (at Room Temperature) | 7000 | psi | — |
Elongation (at Room Temperature) | 5 - 10 | % | — |
Impact Resistance (at Room Temperature) | min. 150 | inch/lb | — |
Water Absorption (for 24 hours) | max. 1 | % | — |
Dielectric Constant (at 25°C, 100Hz) | 4.5 | — | — |
Dielectric Strength (at Room Temperature) | 410 | v/mil | — |
Volume Resistivity (at Room Temperature) | 8 x 10¹⁴ | ohm-cm | — |
Volatile Organic Compounds (at Room Temperature) | 0 | % by weight | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Storage & Handling
- Shelf Life
- 12 Months
- Storage & Handling
- Bring both components to room temperature prior to mixing. Mix 1 part A to 1 part B thoroughly for 30 to 60 seconds.
- Dispense mixed material over properly positioned devices to be glued together. Do not pour more than 1/2” thick as the product may exotherm too high and may boil. As this is a very quick adhesive, you must work quickly to bond the pieces together.
- Parts may be shipped within 24 hours but parts can be moved in 1 hour.