Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
Applications & Uses
- Cure Method
Properties
- Component A
- Component B
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Viscosity | 80000 | cps | — |
| Value | Units | Test Method / Conditions | |
| Viscosity | 80000 | cps | — |
| Value | Units | Test Method / Conditions | |
| Working Time (at 75°F/ 24°C) | 60 | minutes | — |
| Fixture Time (at 75°F/ 24°C) | 10 | hours | — |
| Full Cure (at Room Temperature, Movement) | 10 | hour | — |
| Full Cure (at Room Temperature, For Full Properties) | 24 | hours | — |
| Operating Temperature | -40 to 266 (40 to 130) | °F (°C) | — |
| Density (at Room Temperature, Mixed) | 9.5 (1.15) | lbs/gal (g/cc) | — |
| Flash Point (at Room Temperature) | min. 392 (min. 200) | °F (°C) | — |
| Mix Ratio (Part A:Part B) | 1:1 | — | — |
| Hardness (at Room Temperature) | 70 | — | Shore D |
| Tensile Strength (at Room Temperature, AL to AL) | min. 3,000 | psi | — |
| T-Peel (at Room Temperature) | 25 | pli | — |
| Elongation (at Room Temperature) | 60 | % | — |
| Impact Resistance (at Room Temperature) | min. 150 | inch/lb | — |
| Dielectric Constant (at 25°C, 100Hz) | 4.5 | — | — |
| Dielectric Strength (at Room Temperature) | 410 | v/mil | — |
| Volume Resistivity (at Room Temperature) | 8 x 10⁻¹³ | ohm-cm | — |
| Water Absorption (for 24 hours) | max. 1 | % | — |
| Volatile Organic Compounds (at Room Temperature) | 0 | % by weight | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Storage & Handling
- Shelf Life
- 12 Months
- Storage & Handling
- Bring both components to room temperature prior to mixing. Mix 1 part A to 1 part B by volume or weight thoroughly for 30 seconds minutes.
- Dispense mixed material over properly positioned devices to be glued together. Pre-bleed side by side cartridges the first 3 inches. Allow system to be undisturbed until fixtured.
- Parts may be shipped within 24 hours but parts can be moved in 10 hours.