Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
Impact Strength
UTEC is the best solution compared to other materials because of its remarkable impact strength.
Coefficient of Friction
UTEC is an excellent material for sliding applications where low coefficient of friction properties are required, working as a self-lubricating material.
Chemical Resistance
UTEC is extremely resistant to a wide variety of substances. The material is almost totally inert; therefore, it can be used in the most corrosive or aggressive environments at moderate temperatures. Even at high temperatures, UTEC is resistant to several solvents, except aromatic, halogenated hydrocarbons and strong oxidizing materials, such as nitric acid.
Compatibility tests between a product sample and the chemical environment are strongly recommended to verify satisfactory part performance, at the same conditions, for a period of time equal to the life time expected for each new application. Even substances classified with high attack or absorption characteristics show good practical results.
Abrasion Wear Resistance
Another outstanding UTEC property is the abrasion wear resistance. This makes UTEC suitable for replacing metals in applications that require high abrasion resistance while providing light-weighting benefits.
Processing
It is not possible to process UTEC through conventional extrusion methods or injection or blow molding, because this material does not flow even at temperatures above its melting point. UTEC requires special processing techniques, such as RAM extrusion and compression molding. These processes are generally used to produce semi-finished parts such as rods and sheets. UTEC can be sintered into porous parts (filters) and calendered into porous sheets. It can also be gel processed into fibers or for a variety of battery separator applications.
Those semi-finished parts can then be machined into parts for a wide range of applications. It is possible to use the same machining techniques as those used for wood or metal, such as sawing, milling, planing, drilling and turning. Other conversion processesmay also be used.
Molecular Structure
The UTEC molecular structure has direct impact on its physical and thermal properties as well as processing performance. There are some characterization methods which can be used to measure the molecular weight of polymers. In the case of UHMWPE resins, the viscosity of polymer diluted solutions is widely used for that purpose.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Recommended Uses & Known Applications
Applications which require highest wear resistance - technical parts, RAM extruded/compression molded rods, sheets, and profiles.
Properties
- Physical Form
- Mechanical Properties
Value Units Test Method / Conditions Abrasion Index (Reference ISO 15527 = 100) 76 - Sand slurry - Internal Abrasion Index (Reference Stainless Steel SAE1020 = 100) 20 - Sand slurry - Internal Charpy Impact Strength min. 100 kJ/m² ISO 11542-2 Kinetic Friction Coefficient 0.09 - ASTM D 1894 Notched Izod Impact Strength No break - - Shore D Hardness 64 ISO 868 Hardness 64 Shore D ASTM D 2240 ISO 868 Shore D Hardness (15 sec) 59 ISO 868 Hardness (15 sec) 59 Shore D ISO 868 Static Friction Coefficient 0.1 - ASTM D 1894 Tensile Strength at Break min. 30 MPa ISO 527 Tensile Strength at Yield 17 MPa ISO 527 Ultimate Elongation min. 300 (min. 350) - - - Physical Properties
Value Units Test Method / Conditions Average Molecular Weight 8.0x10⁶ g/mol Internal Method Average Particle Size (Dp50) 130 μm ASTM D 1921 Bulk Density 0.45 g/cm³ ASTM D 1895 Density 0.925 g/cm³ ASTM D 792 Intrinsic Viscosity 28 dL/g ASTM D 4020 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Linear Expansion (Between - 30°C and 100°C) 1.5 10 ^-4/°C ASTM D 696 Heat Deflection Temperature (at 0.45 N/mm²) 79 °C ASTM D 648 Heat Deflection Temperature (at 1.81 N/mm²) 48 °C ASTM D 648 Melting Point 133 °C ASTM D 3418 Specific Heat (at 23°C) 0.48 cal/(g.C) ASTM E 1269 Specific Melt Enthalpy 34 cal/g ASTM D 3418 Thermal Conductivity (at 23°C) 0.4 W/m.k ASTM D 177 Vicat Softening Temperature (at 1kg) 128 °C ISO 306 - Electrical Properties
Value Units Test Method / Conditions Dielectric Constant (at 1KHz) 2.3 - ASTM D 150 Dielectric Strength 900 kV/cm ASTM D 149 Surface Resistivity min. 10¹² ohm ASTM D 257 Volume Resistivity min. 10¹⁴ Ω·cm ASTM D 257 - Other Properties
Value Units Test Method / Conditions Water Absorption 0.01 % ASTM D 570