- DAI-EL G-558 is a bisphenol type cure-incorporated terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which has excellent extrusion processability.
- It offers excellent fuel resistance and is suitable for fuel hoses.
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Soluble in
- Lower ketones and esters
- Physical Properties
- Physical Properties of Vulcanizate
- Note
- *1 The above values are representative and not guaranteed.
- *2 [Formula] DAI-EL G-558: 100 phr, SRF carbon black (N774): 13 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 45min at 160°C, Post cure: 24hrs at 230°C.
- *3 Compression set tested after post cure, while others tested without post cure.
- *4 P-24 O-ring.
Value | Units | Test Method / Conditions | |
Fluorine Content | 69 | mass% | — |
Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 43 | MU | ASTM D1646 |
Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 32 | MU | ASTM D1646 |
Specific Gravity (at 23°C) | 1.87 | — | ASTM D792 |
Value | Units | Test Method / Conditions | |
100% Tensile Stress*² | 2.4 | MPa | ASTM D412 |
Compression Set (70hours at 200°C, 25% Compression*⁴)*² | 28 | % | — |
Elongation (at break)*² | 320 | % | ASTM D412 |
Hardness (at 3 sec)*² | 57 | Shore A | ASTM D2240 |
Hardness (at Peak)*² | 66 | Shore A | ASTM D2240 |
Low Temperature Retraction (TR10)*² | -13 | °C | ASTM D1329 |
Tensile Strength*² | 11.3 | MPa | ASTM D412 |
Safety & Health
- Handling Method / Safety Information
- Be sure to read the notes on SDS and labels before use.
- This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Packaging & Availability
- Packing Specification
20 Kg