- DAI EL G - 565 is a bisphenol type cure incorporated terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which has excellent extrusion processability.
- It offers excellent fuel resistance and is suitable for fuel hoses.
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Soluble in
- Lower ketones and esters
- Physical Properties
- Characteristics
- Physical Properties of Vulcanizate
- Note
- The above values in properties are representative and not guaranteed.
- * [Formula] DAI EL G 565: 100 phr, SRF carbon black (N774): 13 phr, Calcium hydroxide: 6 phr, Magnesium Oxide high active): 3 phr, [Curing condition] Press cure: 45min at 160°C.
| Value | Units | Test Method / Conditions | |
| Fluorine Content | 69 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 39 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 27 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.87 | — | ASTM D792 |
| Value | Units | Test Method / Conditions | |
| Film Appearance | Milky white to pale yellow | — | — |
| Value | Units | Test Method / Conditions | |
| 100% Tensile Stress*² | 2.2 | MPa | ASTM D412 |
| Elongation (at break)*² | 400 | % | ASTM D412 |
| Hardness (at 3sec)*² | 58 | Shore A | ASTM D2240 |
| Hardness (at peak)*² | 68 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -13 | °C | ASTM D1329 |
| Tensile Strength*² | 11.4 | MPa | ASTM D412 |
Safety & Health
- Handling Method / Safety Information
- Be sure to read the notes on SDS and labels before use.
- This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Packaging & Availability
- Packing Specification
20 Kg