- Transparent ultraviolet (UV) curing type optical adhesive based on fluorinated epoxy and fluorinated acrylate resin.
- It is used to connect optical fibers requiring optically optimal refractive index matching as well as adhesion fixing function.
- Highly reliable adhesive with excellent adhesion and workability.
Applications & Uses
- Application Area
- Cure Method
Properties
- Appearance
- Light yellow transparent
- Physical Properties
- Note
- Curing conditions: 5 J/cm2 or 10 J/cm2 UV light was irradiated with a high pressure mercury lamp Fracture mode with bonding strength change is due to glass breakage
- * The above values are representative and not guaranteed.
- * Optodyne UV-1100, UV-2100, UV-3100 contains about 2% antimony compound.
| Value | Units | Test Method / Conditions | |
| Bonding Strength Change (Heat cycle resistance, Pyrex glass, -40~85℃, 90% RH, 6 hour/1cycle, after 100 cycles) | 6.4 | Mpa | — |
| Bonding Strength Change (Heat cycle resistance, Pyrex glass, -40~85℃, 90% RH, 6 hour/1cycle, Initial) | 6.6 | Mpa | — |
| Bonding Strength Change (Heat cycle resistance, Pyrex glass, -40~85℃,90% RH,6 hour/1cycle, after 300 cycles) | 8.7 | Mpa | — |
| Bonding Strength Change (Heat cycle resistance, Pyrex glass, -40~85℃,90% RH,6 hour/1cycle, after 500 cycles) | 7.5 | Mpa | — |
| Bonding Strength Change (Moisture resistance, Pyrex glass, 85℃/85 RH, after 4 weeks) | 7.5 | Mpa | — |
| Bonding Strength Change (Moisture resistance, Pyrex glass, 85℃/85 RH, after 6 weeks) | 7.4 | Mpa | — |
| Bonding Strength Change (Moisture resistance, Pyrex glass, 85℃/85 RH, Initial) | 6.6 | Mpa | — |
| Curing Contraction Rate (Post Curing) | approx. 4 - 5 | % | — |
| Flash Point (Before Curing) | 118 | ℃ | — |
| Glass Transition Temperature (Post Curing) | 145 | ℃ | — |
| Hardness (Post Curing) | 82 | Shore D | — |
| Main Constituents | Epoxy | — | — |
| Mass Decrease Onset Temperature (Post Curing) | 145 | — | TGA |
| Refractive Index (at 23℃, 589nm wavelength) (Post Curing) | 1.457 | — | — |
| Refractive Index (at 23°C) (Before Curing) | 1.435 | — | — |
| Refractive Index (at 25℃, 1320nm wavelength) (Post Curing) | 1.449 | — | — |
| Saturated Moisture Absorption Rate (at 85℃, 85%RH, thickness 3.0mm) (Post Curing) | 2.4 | % | — |
| Saturated Water Absorption Rate (at 23°C, thichness 0.1mm) (Post Curing) | 1.3 | % | — |
| Saturated Water Absorption Rate (at 23°Cx24 hour, thichness 3mm) (Post Curing) | 0.13 | % | — |
| Specific Gravity (at 25°C, Before Curing) | 1.36 | — | — |
| Specific Gravity (Post Curing) | 1.42 | — | — |
| Temperature of 5% Weight Loss (Post Curing) | 313 | ℃ | TGA |
| Transmittance (at 1300nm wavelength,Thickness 0.1mm) (Post Curing) | 93.4 | % | — |
| Transmittance (at 500~1600nm wavelength,Thickness 0.1mm) (Post Curing) | min. 90 | % | — |
| Viscosity (at 25°C, Before Curing) | 230 | mPa.s | — |
| Young Modulus (Post Curing) | 2.7×10⁹ | pascal | — |
Safety & Health
- Handling Method / Safety Information
- Be sure to read the notes on SDS and labels before use.
- This product is intended for general industry use and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Packaging & Availability
- Packaging Type
- Packing Specification
- 5g (tube)
- 50g (tube)