- Polyflon PTFE ED - 3200 grade is a water based PTFE topcoat.
- Polyflon PTFE ED - 3293SW1R makes a grayish brown topcoat layer displaying conductivity and non stick property.
- It is good for office automation equipments.
Applications & Uses
- Application Area
Properties
- Physical Form
- Physical Properties
- Characteristics
- Physical Properties of Coated Film
- Note
1. The coating film was evaluated with a test piece below.
- Substrate: Aluminum plate roughened with Tosa Emely Extra #80/#100=50/50
- Primer: ED 1939D21R, approximately 10μm thick
- Topcoat: Approximately 10 15μm thick
2. The above values in properties are typical and not guaranteed.
| Value | Units | Test Method / Conditions | |
| pH | 9 | — | — |
| Solid Content | 40 | mass% | — |
| Specific Gravity of Coating | approx. 1.3 - 1.4 | — | — |
| Viscosity | 260 | cP | — |
| Value | Units | Test Method / Conditions | |
| Film Appearance | Grayish brown | — | — |
| Value | Units | Test Method / Conditions | |
| Contact Angle (Hexadecane, at 25°C) | 45 - 55 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 115 - 125 | Degree | Contact Angle Meter |
| Cross Cut Adhesion (Stripping with cellophane tape,10 times) | 100/100 | — | JIS K5400 8.5 |
| Pencil Hardness (at 200°C, Stripping hardness of base material) | 2B - B | — | JIS K6894 |
| Pencil Hardness (at 25°C, Stripping hardness of base material) | F - 2H | — | JIS K6894 |
| Surface Electrical Resistance (Measured a film which was made on a glass plate with Hiresta HT 450, 10~500V,10sec) | 1.0×10² - 9.9×10⁷ | Ω | — |
| Taber Abrasion (at 25°C, CS 17, 1kg, 1000 rounds) | 2 - 4 | mg/1000 rounds | — |
Safety & Health
- Handling Method / Safety Information
- Be sure to read the notes on SDS and labels before use.
- This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.