| Value | Units | Test Method / Conditions | |
| Tensile Modulus (1 mm/min) | 3700 / 1700 | MPa | ISO 527 |
| Tensile Stress at Yield (50 mm/min) | 85 / 50 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 15 / min. 50 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 125 / 60 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 3400 / 1600 | MPa | ISO 178 |
| Charpy Notched Impact Strength (+23 °C) | 4 / 8.5 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (-30°C) | 3.5 / - | kJ/m2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength (+23 °C) | 75 / NB | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (+23 °C) | 3.5 / 8 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (+23 °C) | 65 / 125 | kJ/m2 | ISO 180/1U |
| Value | Units | Test Method / Conditions | |
| Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 1.1 - 1.3 | % | ISO 294-4 / 2577 |
| Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 1.1 - 1.3 | % | ISO 294-4 / 2577 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.80 MPa) | 80 | °C | ISO 75 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 210 | °C | ISO 75 |
| Melting Point (DSC) | 262 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50°C/h - 50N) | 240 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index - CTI (Solution A) | 600 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Flammability (1.5 mm) | V-0 | class | UL 94 |
| Glow Wire Ignition Temperature - GWIT (1 - 3 mm) | 750 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index - GWFI (1 - 3 mm) | 960 | °C | IEC 60695-2-12 |
| Flammability (0.8 mm) | V-0 | - | UL 94 |
| Value | Units | Test Method / Conditions | |
| Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | - |
| Recommended Melt Temperature | 260 - 290 | °C | - |
| Recommended Mold Temperature | 60 - 80 | °C | - |
| Drying Temperature | 75 - 85 | °C | - |