LNP™ THERMOCOMP™ Compound RF0039S

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Cost Effective,

Flame Retardant,

Good Mold Release,

Heat Stabilized,

High Modulus,

High Stiffness,

UL Listed

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Construction Applications,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Fishing Lines,

Fishing Nets,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Oil/Gas Applications,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	100	MPa	ASTM D638
Tensile Stress (Break) ¹¹	98	MPa	ISO 527
Tensile Strain (Break) ¹¹	2.9	%	ISO 527
Tensile Strain (Break) ¹¹	3	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	6060	MPa	ASTM D638
Flexural Stress ¹¹	160	MPa	ASTM D790
Flexural Stress ¹¹	164	MPa	ISO 178
Flexural Modulus ¹¹	6000	MPa	ISO 178
Flexural Modulus ¹¹	5170	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	6300	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.48	g/cm³	ISO 1183
Density ¹¹	1.487	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.49	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.89	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.9	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.29	%	ISO 294

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	251	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	226	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	219	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	105	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	115	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index (UL, PLC) ¹¹	3	PLC Code	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 3	mm	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 1.7	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 3	mm	UL 746A
High Ampere Arc Ignition (PLC 1) ¹¹	min. 1.7	mm	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	1	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	7	PLC Code	ASTM D495

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	523	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	42	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	5	J	ASTM D3763
Multi-Axial Impact ¹¹	1	J	ISO 6603
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	38	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	275 - 290	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 1.7	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America