Products

Ebalta MG 453 GF is processed on a two-component low pressure device. After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Release agent – please see category release agent

The product group ebalta SG 2000 consists of high-quality, nearly odorless two-component-Polyurethane casting resins without mixed in filler. The filler is stirred in when the components are mixed. There are different resin components available, which are processed with one hardener. The single types differ in potlife and curing time.

ebalta MG 321 FR is processed on a two-component low pressure device. After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Nitrocellulose lacquers have a better adhesion on polyurethane surfaces than on acryllacquer- systems. As release agent you can use our T 03-01. MG 321 FR beige fire behavior according to UL 94, 3 mm thickness V0 With MG 883 the potlife of MG 321 FR beige can be set up to 120 secs. MG 321 FR-S beige/ black - Approved according to UL 94 - File E191776 Vol. 1 fire behavior based on UL 94, 3 mm thickness V0 and 5VA

ebalta SG 150 is a four component acryl casting resin. It consists of 2 liquid components and a hardener powder. Both liquid components are filled with the 1,5 amount in ppw of special aluminum powder. The resin cures within 20-30 minutes to well heat-conducting, heat-resistant molds. The cured molds are very well workable by machines. The structure is extremely dense and the machined areas have an aluminum-like appearance. It is possible to cast any quantity, which can be mixed in one or more containers. Altercating or casting in layers is not possible. Therefore it is very important to determine the casting volume exactly in order to avoid that the mixed quantity is too small. Since the hardener powder is hygroscopic, always seal it air-tight. We recommend to sieve it before each use. Linear shrinkage as per mixture listed in the data sheet. Room temperature and starting temperature of resin components are 21°C as per measurement. For other temperatures or a different content of aluminum powder, shrinkage might also be different.

Ebalta LH 30 / Resin+Hardener is a two components epoxy laminating resin, precuring at room temperature and, depending on postcuring, can be used till 175°C. Since this laminating resin system contains no fillers, it has got good wetting properties and makes a high glass fabric content possible. This leads to a low coefficient of thermal expansion and high strength. Together with aluminum granules, ebalta LH 28-1 is suitable for back filling of heat resistant molds and molding tools.

Ebalta GM 727 is a well castable two components polyurethane casting resin, curing slowly at room temperature. This casting resin is particularly suitable for solid casting of dimensionally accurate large-volume models with high temperature resistance. Due to low mixing viscosity of GM 727 you can add 70% filler F-B and about 50% plastic granules to reduce shrinkage to approx. 0.05%.

Ebalta GM 979 is an easy-to-handle-2components-polyurethane casting compound which shows very low adhesive properties compared to molding sand. Due to its high abrasion resistance, GM 979 is especially suitable for foundry patterns, which have to resist to abrasive wear by molded sand. GM 979 even keeps its high mechanical strength when using molding sands with higher temperatures.

Ebalta LH 28-1 / TM is a two components epoxy laminating resin, precuring at room temperature and, depending on postcuring, can be used till 175°C. Since this laminating resin system contains no fillers, it has got good wetting properties and makes a high glass fabric content possible. This leads to a low coefficient of thermal expansion and high strength. Together with aluminum granules, ebalta LH 28-1 is suitable for back filling of heat resistant molds and molding tools. At room temperature the curing takes 7 days and the material can only be used for applications till 60°C.

Ebalta SG 2000 / Comp. A+B consists of high-quality, nearly odorless two-component-Polyurethane casting resins without mixed in filler. The filler is stirred in when the components are mixed. There are different resin components available, which are processed with one hardener. The single types differ in potlife and curing time.