Elix - ABS 118HF - ELIX Polymers - Injection Molding

Identification & Functionality

Features & Benefits

Applications & Uses

Markets: Consumer Goods,
Electrical & Electronics
Applications: Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
Other Devices & Assemblies
Consumer Goods — Other Consumer Goods Applications
Electrical & Electronics — Parts & Components
Housings & Enclosures
Plastics & Elastomers End Uses: Appliances,
Consumer Applications,
Electrical/Electronic Applications,
Housings
Plastics & Elastomers Processing Methods: Injection Molding

Properties

	Value	Units	Test Method / Conditions
Elongation at Break (23°C/50% Relative Humidity, 5 mm/min)	34	%	ASTM D 638
Elongation at Break (23°C/50% Relative Humidity, 50 mm/min)	34	%	ISO 527-1,2
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min)	328000	psi	ASTM D 638
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min)	2260	MPa	ISO 527-1,2
Yield Stress (23°C/50% Relative Humidity, 5 mm/min)	39	MPa	ASTM D 638
Yield Stress (23°C/50% Relative Humidity, 50 mm/min)	42	MPa	ISO 527-1,2
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min)	66	MPa	ISO 178
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min)	341000	psi	ASTM D 790
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min)	2350	MPa	ISO 178
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”)	95	J/m	ASTM D 256
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”)	180	J/m	ASTM D 256
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity)	14	kJ/m2	ISO 180-1A
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity)	7	kJ/m2	ISO 180-1A
Ball Indentation Hardness (23°C/50% Relative Humidity)	92	N/mm2	ISO 2039-1

	Value	Units	Test Method / Conditions
Melt Flow Rate - MFR (230°C, 3.8Kg)	15	g/10min	ASTM D1238
Melt Volume Flow Rate - MVFR (220°C, 10Kg)	57	cm3/10min	ISO 1133
Molding Shrinkage - Normal (60X60X2 mm)	0.5-0.7	%	ISO 294-4
Molding Shrinkage - Parallel (60X60X2 mm)	0.5-0.7	%	ISO 294-4
Density (25°C)	1.03	g/cm3	ISO 1183-1

	Value	Units	Test Method / Conditions
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C)	0.9	10-4/K	ISO 11359 -1,2
Deflection Temperature Under Load (0.45 Mpa)	101	°C	ISO 75-1,2
Deflection Temperature Under Load (1.80 Mpa)	98	°C	ISO 75-1,2
Vicat Softening Temperature (50N, 50°C/h)	217	ºF	ASTM D 1525
Vicat Softening Temperature (B50, 50°C/h)	103	°C	ISO 306

Regulatory & Compliance

Packaging & Availability

Elix™ ABS 118HF