Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
- Processing Information (Injection Molding)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Yield Stress (at 23°C/50 % r. h.,50mm/min) | 50.5 | MPa | ISO 527-1,-2 |
| Tensile Stress at Break (at 23°C/50 % r. h.,50mm/min) | 36.5 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (at 23°C/50 % r. h.,50mm/min) | min. 15 | % | acc. ISO 527-1,-2 |
| Tensile Modulus (at 23°C/50 % r. h.,1mm/min) | 2550 | MPa | ISO 527-1,-2 |
| Flexural Strength (at 23°C/50 % r. h.,2mm/min) | 75 | MPa | ISO 178 |
| Flexural Modulus (at 23°C/50 % r. h.,2mm/min) | 2600 | MPa | ISO 178 |
| Izod Notched Impact Strength (at 23°C/50 % r. h.) | 15 | kJ/m² | ISO 180-1A |
| Izod Notched Impact Strength (at -30°C/50 % r. h.,) | 7 | kJ/m² | ISO 180-1A |
| Yield Strain (at 23°C/50 % r. h.,50mm/min) | 2.6 | % | ISO 527-1,-2 |
| Nominal Strain at Break (at 23°C/50 % r. h.,50mm/min) | 20 | % | ISO 527-1,-2 |
| Charpy Impact Strength (at 23°C/50 % r. h.) | 124 | kJ/m² | ISO 179-1eU |
| Charpy Impact Strength (at -30°C/50 % r. h.,) | 100 | kJ/m² | ISO 179-1eU |
| Charpy Notched Impact Strength (at 23°C/50 % r. h.,) | 16 | kJ/m² | ISO 179-1eA |
| Charpy Notched Impact Strength (at -30°C/50 % r. h.,) | 7 | kJ/m² | ISO 179-1eA |
| Ball Indentation Hardness | 106 | N/mm² | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Temperature Of Deflection Under Load (1.80Mpa) | 94 | °C | ISO 75-1,-2 |
| Temperature Of Deflection Under Load (0.45Mpa) | 98 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (50N; 120°C/h) | 101 | °C | ISO 306 |
| Vicat Softening Temperature (50N; 50°C/h) | 98 | °C | ISO 306 |
| Coefficient of Linear Lhermal Expansion, Parallel (at 23 to 55°C) | 0.78 | 10⁻⁴/K | ISO 11359-1,-2 |
| Coefficient of Linear Thermal Expansion, Transverse (at 23 to 55°C) | 0.81 | 10⁻⁴/K | ISO 11359-1,-2 |
| Burning Behavior (UL 94 (1.6 mm)) | HB | Classs | UL 94 |
| Glow Wire Test (GWFI) (2.0 mm) | 650 | °C | IEC 60695-2-12 |
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (23°C/50 % r. h.,100 Hz) | 3.04 | — | IEC 60250 |
| Relative Permittivity (23°C/50 % r. h.,1 Mhz) | 2.82 | — | IEC 60250 |
| Dissipation Factor (at 23°C/50 % r. h.,100 Hz) | 53 | 10⁻⁴ | IEC 60250 |
| Dissipation Factor (at 23°C/50 % r. h.,1 MHz) | 96 | 10⁻⁴ | IEC 60250 |
| Volume Resistivity (23°C/50 % r. h.) | 2 × 10¹⁴ | Ohm·m | IEC 60093 |
| Surface Resistivity (23°C/50 % r. h.) | 2E+17 | Ohm | IEC 60093 |
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.055 | g/cm³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Melt Temperature | 240 | °C | ISO 294 |
| Mold Temperature | 70 | °C | ISO 294 |
| Injection Velocity | 240 | mm/s | ISO 294 |
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 220°C; 10 Kg) | 20 | cm³/(10 min) | ISO 1133 |
| Molding Shrinkage, Parallel (150X105X3; 500 Bar) | 0.5 | % | acc. ISO 2577 |
| Molding Shrinkage, Normal (150X105X3; 500 Bar) | 0.5 | % | acc. ISO 2577 |
Regulatory & Compliance
- Certifications & Compliance