Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Recommended Printing Conditions
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.13 - 1.15 | g/cm3 | ASTM D792 |
| Water Adsorption (24h - 23°C) | 1.3 | % | ASTM D570 |
| Linear Mould Shrinkage | 1.9 - 2.0 | % | — |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min.) | 79.0 | MPa | ASTM D638 |
| Elongation At Break (50 mm/min.) | 55.0 | % | ASTM D638 |
| Flexural Modulus (1.3 mm/min.) | 3200.0 | MPa | ASTM D790 |
| Impact Strength (Notched (23°C - 3.2 mm) | min. 40 | J/m | ASTM D256 |
| Rockwell Hardness | 118.0 | Scala R | ASTM D785 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Point (49N x 120°C/h) | min. 235 | °C | ASTM D1525 |
| Melting Point | 255.0 | °C | ASTM D2117 |
| Continuos Exercise Temperature | 90.0 | °C | — |
| Value | Units | Test Method / Conditions | |
| Glow Wire Test (S=2 mm) | 650.0 | °C | IEC 695-2-1 |
| Flammability (S=1.6 mm) | HB | Classe | UL 94 |
| Flammability (S=3.2 mm) | HB | Classe | UL 94 |
| Value | Units | Test Method / Conditions | |
| Cylinder Temperature | 250 - 270 | °C | — |
| Mold Temperature | 60 - 90 | °C | — |
| Dry Temperature (2-4 h) | 80 - 100 | °C | — |
| Injection Speed | Medio-alta | — | — |