Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Features
- 100% Solids
- High Impact Strength
- Excellent Tensile Strength
- 1 to 1 By Volume
- No MOCA or TDI
- Quick Setting
Applications & Uses
- Markets
- Application Method
Properties
- Physical Properties
Value | Units | Test Method / Conditions | |
Hardness | 80.0 | Shore D | — |
Modulus (100%) | 4250.0 | psi | — |
Tensile Strength (Ultimate) | 8110.0 | psi | — |
Elongation | 195.0 | % | — |
Tear Strength (“Die C”) | 115.0 | lbs/in | — |
Compression Set (Method A) | 10.0 | — | — |
Impact Resistance | 12.0 | ft-lbs/in | — |
Heat Deflection Temperature (HDT) | 195.0 | °F | — |
Technical Details & Test Data
- Processing Parameters
Process Polyol 3020B at 100 to 150 degrees F.
Melt Isocyanate 680A if frozen at 100 degrees F., otherwise use at 75-120 degrees F.
Mold Temperature: 65 to 110 degrees F.
Mix ratio: 1 part Polyol 3020B to 1 part Isocyanate 680A by volume or 91.20 parts polyol to 100 parts Isocyanate 680B by weight.
Degas mixture if possible or pre-degas Polyol in dispensing equipment prior to casting.
Demold 10-15 minutes with maximum process and mold temperature. Catalyst may also be used to shorten demold time.
Post Cure: 16-24 hours @ 75 degrees F.
Storage & Handling
- Storage and Pot Life
Systems should be stored unopened in air tight containers at 60-90 degrees F. Partially emptied containers should be swept free of atmospheric moisture with dry nitrogen before sealing.
Pot life: (200g mass) (100 degrees F) 10 to 15 minutes.