Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
- Compounding
- Injection Molding
Features & Benefits
- Features
- Good Weather Resistance
- High Flow
- Low Molecular Weight
Applications & Uses
- Plastics & Elastomers Processing Methods
- Uses
- Blending
- Compounding
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Optical Properties
- Impact Properties
- Hardness
Value | Units | Test Method / Conditions | |
Flexural Modulus | 3440 | MPa | ASTM D790 |
Flexural Strength | 66.2 | MPa | ASTM D790 |
Tensile Elongation (at Break) | 1.9 | % | ASTM D638 |
Tensile Elongation (at Yield) | 1.5 | % | ASTM D638 |
Tensile Modulus | 4090 | MPa | ASTM D638 |
Tensile Strength (at Break) | 60.2 | MPa | ASTM D638 |
Tensile Strength (at Yield) | 48.8 | MPa | ASTM D638 |
Value | Units | Test Method / Conditions | |
Density | 1.07 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate | 38 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (at 0.45 MPa, Unannealed) | 97.8 | °C | ASTM D648 |
Deflection Temperature Under Load (at 1.8 MPa, Unannealed) | 86.7 | °C | ASTM D648 |
Vicat Softening Temperature | 103 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Yellowness Index | 16 | YI | ASTM D1925 |
Value | Units | Test Method / Conditions | |
Notched Izod Impact (at -30°C) | 23 | J/m | ASTM D256 |
Notched Izod Impact (at 23°C) | 12 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Rockwell Hardness | 106 | R-Scale | ASTM D785 |