Goldsmith & Eggleton

G&E 9007 BMB is mechanically mixed SBR Black masterbatch. This material can be used to replace similar co-precipitated masterbatch in most applications. G&E 9007 contains 100 parts SBR, 52 parts of N-234 series carbon black, and 10 parts Highly Napthenic Oil.

G&E 1815 BMB is mechanically mixed SBR Black masterbatch. This material can be used to replace SBR-1815 coprecipitated masterbatch in most applications. G&E 1815 contains 100 parts of non-staining SBR, 75 parts of N-300 series carbon black, and 50.0 parts Napthenic Oil.

G&E 1605 BMB is mechanically mixed SBR Black master batch. This material can be used to replace SBR-1605 co-precipitated master batch in most applications. G&E 1605 contains 100 parts of non-staining SBR and 50 parts of N-500 series Carbon Black.

G&E 565 is produced from feedstocks carefully selected for uniform viscosity, ethylene propylene ratio and 3rd monomer. The feedstocks are chosen to produce a blended EPDM Polymer which has a high ethylene content, medium mooney and high diene. G&E Blended EPDM 565 can be blended with prime EPDM polymers to reduce compound costs in extruded, calendered and molded applications.

G&E Blended HIIR is produced by carefully combining selected feedstocks for uniform viscosity and halogen Content. G&E Blended Halogenated Butyl is excellent for cost reductions in applications such as non-cured tapes, construction adhesives, caulks, inner liners, and re-treader sundries. G&E Blended Halogenated Butyl can be used as a direct partial replacement of prime Butyl and halogenated Butyl Rubber.

G&E 1848 BMB is mechanically mixed SBR Black masterbatch. This material can be used to replace SBR-1848 coprecipitated masterbatch in most applications. G&E 1848 contains 100 parts SBR, 82.5 parts of N-300 series carbon black, and 62.5 parts Highly Aromatic Oil.

G&E 1805 BMB is mechanically mixed SBR Black masterbatch. This material can be used to replace SBR-1805 coprecipitated masterbatch in most applications. G&E 1805 contains 100 parts of non-staining SBR, 75 parts of N-330 series carbon black, and 37.5 parts napthenic oil.

G&E 254 is produced from feedstocks carefully selected for uniform viscosity, ethylene propylene ratio, and 3rd monomer. The feedstocks are chosen to produce a blended EPDM Polymer which has a medium ethylene content, medium diene content, and low mooney. G&E Blended EPDM 254 can be blended with prime EPDM polymers to reduce compound costs in extruded, calendered and molded applications.

G&E Blended PMSB is made from brominated isobutylene paramethylstyrene feedstocks selected for mooney, bromine and paramethylstyrene content to achieve a uniformly-blended polymer. G&E Blended PMSB is excellent for cost reductions in applications such as innerliners, non-cured tapes, construction adhesives and caulks. G&E Blended PMSB can be used as a direct partial replacement of prime butyl and halogenated butyl rubber.