Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Other Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 100 / 60 | MPa | ISO 527 |
| Tensile Modulus | 4500 / 2500 | MPa | ISO 527 |
| Strain at break | 5.0/20.0 | % | ISO 527 |
| Flexural modulus, 23° | 3900 / 2200 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 4.0/9.0 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 45 / 130 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 5.0/8.0 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 180 / 90 | MPa | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 60 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 60 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 2 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 8/1 | % | ISO 294-4 |
| Molding shrinkage - parallel | 0.8 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - normal | 1.2 / * | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 9 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 2.7 | % | ISO 62 |
| Density | 1190 / - | kg/m3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion (parallel) | 20 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 120 / * | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 170 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 170 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 200 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 200 / * | °C | ISO 306 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index - CTI | 525 | V | IEC 60112 |
| Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
| Value | Units | Test Method / Conditions | |
| Flammability - Glow Wire Test | 650 | °C | IEC-60695-2-12 |
| Value | Units | Test Method / Conditions | |
| Water absorption | 9 / * | % | Sim. to ISO 62 |
| Humidity absorption | 2.7 / * | % | Sim. to ISO 62 |