Tarnamid® T-27 GF25 MT15

Identification & Functionality

Additives Included

Heat Stabilizer

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

Mineral

Polymer Name

Polyamide 6 (PA 6)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Heat Stabilized

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Other Automotive Applications

Building & Construction — Building Materials

Other Building Materials

Electrical & Electronics — Devices & Assemblies

Other Devices & Assemblies

Consumer Goods — Housewares

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Construction Applications,

Electrical/Electronic Applications,

Household Goods

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

IEC 60695-11-10 HB

Physical Form

Granules,

Solid

Flame Rating

IEC 60695-11-10 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength	135 / 100	MPa	ISO 527
Tensile Modulus	11300 / 8600	MPa	ISO 527
Strain at break	4.0/5.0	%	ISO 527
Flexural modulus, 23°	10200 / 7800	MPa	ISO 178
Charpy notched impact strength (-30°)	5.0/5.0	kJ/m2	ISO 179/1eA
Charpy notched impact strength (+23°)	6.0/9.0	kJ/m2	ISO 179/1eA
Charpy impact strength (+23°)	55 / 65	kJ/m2	ISO 179/1eU
Charpy impact strength (-30°)	45 / 45	kJ/m2	ISO 179/1eU
Izod notched impact strength, +23°	7.0/8.0	kJ/m2	ISO 180/1A
Ball indentation hardness	220 / 150	MPa	ISO 2039-1

Physical Properties

	Value	Units	Test Method / Conditions
Melt Volume Flow Rate - MVR (275°C/5.0 kg)	30	cm3/10min	ISO 1133
Melt Volume Flow Rate - MVR (275°C/5 kg)	30 / *	cm3/10 min	ISO 1133
Molding Shrinkage - Paralell (60×60×2 mm)	0	%	ISO 294-4
Molding Shrinkage - Paralell (60×60×2 mm)	9	%	ISO 294-4
Molding Shrinkage - Paralell (60×60×2 mm)	3/0	%	ISO 294-4
Molding shrinkage - parallel	0.3 / *	%	ISO 294-4, 2577
Molding shrinkage - normal	0.9 / *	%	ISO 294-4, 2577
Water Absorption (23/sat.)	7	%	ISO 62
Moisture Absorption (23°C/50% RH)	2	%	ISO 62
Density	1440 / -	kg/m3	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Linear Thermal Expansion (parallel)	10 / *	E-6/K	ISO 11359-1/-2
Coefficient of Linear Thermal Expansion (normal)	90 / *	E-6/K	ISO 11359-1/-2
Delfection Temperature Under Load (1.8 MPa)	210	°C	ISO 75-1,-2
Temperature of deflection under load (1.80 Mpa)	210 / *	°C	ISO 75-1/-2
Melting Point (DSC)	221	°C	ISO 11357-1
Vicat Softening Temperature (50 N)	215	°C	ISO 306
Melting temperature (10°C/min)	221 / *	°C	ISO 11357-1/-3
Thickness tested	3.2 / *	mm	—
Vicat softening temperature	215 / *	°C	ISO 306
Burning Behavior at thickness	HB / *	class	IEC 60695-11-10

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index - CTI	525	V	IEC 60112
Surface Resistivity	1.0e+15	ohm	STN 34 6460
Volume Resistivity	1.0e+15	ohm.m	ASTM D 257

Other Properties

	Value	Units	Test Method / Conditions
Water absorption	7 / *	%	Sim. to ISO 62
Humidity absorption	2 / *	%	Sim. to ISO 62