Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus | 1800 / 700 | MPa | ISO 527 |
Yield stress | 50 / 32 | MPa | ISO 527 |
Strain at Break | min. 50 / min. 50 | % | ISO 527 |
Flexural modulus, 23° | 1600 / 500 | MPa | ISO 178 |
Charpy impact strength (-30°) | N / N | kJ/m2 | ISO 179/1eU |
Charpy impact strength (+23°) | N / N | kJ/m2 | ISO 179/1eU |
Charpy notched impact strength (-30°) | 30 / - | kJ/m2 | ISO 179/1eA |
Charpy notched impact strength (+23°) | 50 / 80 | kJ/m2 | ISO 179/1eA |
Izod notched impact strength, +23° | 50 / 75 | kJ/m2 | ISO 180/1A |
Ball indentation hardness | 95 / 65 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 60 | cm3/10min | ISO 1133 |
Melt Volume Flow Rate - MVR (275°C/5 kg) | 60 / * | cm3/10 min | ISO 1133 |
Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 7/2 | % | ISO 294-4 |
Molding shrinkage - normal | 2.1 / * | % | ISO 294-4, 2577 |
Molding shrinkage - parallel | 1.7 / * | % | ISO 294-4, 2577 |
Water Absorption (23/sat.) | 7 | % | ISO 62 |
Moisture Absorption (23°C/50% RH) | 2.2 | % | ISO 62 |
Density | 1080 / - | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (parallel) | 130 / * | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (normal) | 160 / * | E-6/K | ISO 11359-1/-2 |
Delfection Temperature Under Load (1.8 MPa) | 55 | °C | ISO 75-1,-2 |
Temperature of deflection under load (1.80 Mpa) | 55 / * | °C | ISO 75-1/-2 |
Melting Point (DSC) | 221 | °C | ISO 11357-1 |
Vicat Softening Temperature (50 N) | 160 | °C | ISO 306 |
Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
Thickness tested | 3.2 / * | mm | — |
Vicat softening temperature | 160 / * | °C | ISO 306 |
Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 600 | V | UL 746 |
Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Value | Units | Test Method / Conditions | |
Water absorption | 7 / * | % | Sim. to ISO 62 |
Humidity absorption | 2.2 / * | % | Sim. to ISO 62 |