Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 V0
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus | 3700 / 1400 | MPa | ISO 527 |
Yield stress | 80 / 45 | MPa | ISO 527 |
Flexural modulus, 23° | 3200 / 1200 | MPa | ISO 178 |
Strain at Break | 20 / min. 50 | % | ISO 527 |
Charpy impact strength (+23°) | 80 / N | kJ/m2 | ISO 179/1eU |
Charpy notched impact strength (+23°) | 3.0/9.0 | kJ/m2 | ISO 179/1eA |
Izod notched impact strength, +23° | 3.0/8.0 | kJ/m2 | ISO 180/1A |
Ball indentation hardness | 150 / 60 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 160 | cm3/10min | ISO 1133 |
Melt Volume Flow Rate - MVR (275°C/5 kg) | 160 / * | cm3/10 min | ISO 1133 |
Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 6 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 5/1 | % | ISO 294-4 |
Molding shrinkage - parallel | 1.5 / * | % | ISO 294-4, 2577 |
Molding shrinkage - normal | 1.6 / * | % | ISO 294-4, 2577 |
Water Absorption (23/sat.) | 9.5 | % | ISO 62 |
Moisture Absorption (23°C/50% RH) | 2.5 | % | ISO 62 |
Density | 1180 / - | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (parallel) | 80 / * | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (normal) | 100 / * | E-6/K | ISO 11359-1/-2 |
Delfection Temperature Under Load (1.8 MPa) | 60 | °C | ISO 75-1,-2 |
Temperature of deflection under load (1.80 Mpa) | 60 / * | °C | ISO 75-1/-2 |
Melting Point (DSC) | 221 | °C | ISO 11357-1 |
Vicat Softening Temperature (50 N) | 195 | °C | ISO 306 |
Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
Thickness tested | 0.8 / * | mm | — |
Vicat softening temperature | 195 / * | °C | ISO 306 |
Burning Behavior at thickness | V-0 / * | class | IEC 60695-11-10 |
Burning Behavior at 1.5 mm nominal thickness | V-0 / * | class | IEC 60695-11-10 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 600 | V | UL 746 |
Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Value | Units | Test Method / Conditions | |
Flammability - Glow Wire Test | 960 | °C | IEC-60695-2-12 |
Value | Units | Test Method / Conditions | |
Water absorption | 9.5 / * | % | Sim. to ISO 62 |
Humidity absorption | 2.5 / * | % | Sim. to ISO 62 |