Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 75 / 50 | MPa | ISO 527 |
Tensile Modulus | 7000 / 4400 | MPa | ISO 527 |
Strain at break | 4.0/4.0 | % | ISO 527 |
Flexural modulus, 23° | 5900 / 3300 | MPa | ISO 178 |
Charpy notched impact strength (+23°) | 3 / 3.5 | kJ/m2 | ISO 179/1eA |
Charpy impact strength (-30°) | 40 / 40 | kJ/m2 | ISO 179/1eU |
Charpy impact strength (+23°) | 45 / 50 | kJ/m2 | ISO 179/1eU |
Charpy notched impact strength (-30°) | 3.0/3.0 | kJ/m2 | ISO 179/1eA |
Izod notched impact strength, +23° | 5 / - | kJ/m2 | ISO 180/1A |
Ball indentation hardness | 160 / 105 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 60 | cm3/10min | ISO 1133 |
Melt Volume Flow Rate - MVR (275°C/5 kg) | 60 / * | cm3/10 min | ISO 1133 |
Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 7 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 3/0 | % | ISO 294-4 |
Molding shrinkage - parallel | 0.3 / * | % | ISO 294-4, 2577 |
Molding shrinkage - normal | 0.7 / * | % | ISO 294-4, 2577 |
Density | 1350 / - | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Delfection Temperature Under Load (1.8 MPa) | 120 | °C | ISO 75-1,-2 |
Temperature of deflection under load (1.80 Mpa) | 120 / * | °C | ISO 75-1/-2 |
Melting Point (DSC) | 221 | °C | ISO 11357-1 |
Vicat Softening Temperature (50 N) | 200 | °C | ISO 306 |
Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
Thickness tested | 3.2 / * | mm | — |
Vicat softening temperature | 200 / * | °C | ISO 306 |
Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 600 | V | UL 746 |
Surface Resistivity | 1.00E+12 | ohm | IEC 60093 |
Volume Resistivity | 1000000000000.0 | ohm.m | IEC 60093 |
Value | Units | Test Method / Conditions | |
Flammability - Glow Wire Test | 650 | °C | IEC-60695-2-12 |
Packaging & Availability
- Country Availability
- Regional Availability