- Superior chemical resistance
- Excellent exterior weathering durability
- Excellent humidity resistance
- Contains n-methyl pyrrolidone co-solvent
Applications & Uses
- Applications
- Application Method
- Coating Type
- Suggested Uses
HD-6000 was developed for use with water-dispersible, isocyanate crosslinkers such as Bayer’s Bayhydur 302 or Perstrop’s Easaqua X D 401 / M 501. The product, when crosslinked provides tough, chemical resistant, glossy coatings which may be applied to a variety of substrates including concrete, metals, plastics and wood materials. This product exhibits superior chemical resistance, while maintaining excellent flexibility and gloss retention characteristics.
- Product Application
HD-6000 crosslinked with water-dispersible isocyanates may be spray applied using single-component equipment. The workable potlife is approximately 3 hours at the suggested crosslinker ratio of 2.0 to 1.0 NCO / OH.
- Curing
HD-6000, crosslinked with a water dispersible isocyanate, will dry to a hard film in 30 minutes at ambient room temperature (65 - 70°F) and humidity (RH 50%). Ultimate cured properties will take about 3 -5 days to develop. If heat is available, the ultimate properties can be attained in shorter time. Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties..
Properties
- Physical Form
- Physical Properties
- Impact Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 34 - 36 | % | — |
| Viscocity | 50 - 500 | cPs | — |
| pH | 7.5 - 10.0 | — | — |
| Density | 8.8 | lbs/gal | — |
| Volatile Organic Compounds (as supplied) | 126.0 | gm/l | — |
| OH Equivalent Wieight | 3100.0 | — | — |
| Value | Units | Test Method / Conditions | |
| Elongation (at 20 inch/min) | 230.0 | % | — |
| Tensile Strength (at 20 inch/min) | 7000.0 | psi | — |
| 100% Modulus (at 20 inch/min) | 4850.0 | psi | — |
| 200% Modulus (at 20 inch/min) | 6800.0 | psi | — |