Knowde Enhanced TDS
Identification & Functionality
- Carrier
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
Applications & Uses
- Markets
- Applications
- Application Method
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Product Applications
- L-2255 can be used as supplied or blended with vinyl acetate/ethylene, styrene butadiene and acrylic emulsions.
- The rheology of L-2255 may be modified with associative or acrylic thickeners for knife-over-roll or similar methods.
Properties
- Physical Form
- Physical Properties
- Mechanical Properties (TPE)
Value | Units | Test Method / Conditions | |
Solids | 47 - 49 | % | — |
Viscosity | 100 - 1000 | cps | Brookfield RVT, speed. 3,100 rpm |
pH | 7.0 - 9.5 | — | — |
Density | 8.75 | lbs/gal | — |
VOC Content (as supplied) | 10 | gm/l | — |
Softening Point | 240 | °F | — |
Value | Units | Test Method / Conditions | |
Elongation | 580 | % | — |
Tensile Strength | 3000 | psi | — |
100% Modulus | 800 | psi | — |
200% Modulus | 1050 | psi | — |
300% Modulus | 1370 | psi | — |
Technical Details & Test Data
- Curing
- L-2255 will dry to a tack-free film in 10 minutes at 200°F. Heat activation will occur between 235 – 245°F.
- L-2255 may be crosslinked with polyaziridines, water dispersible polyisocyanates, epoxy silanes or low temperature melamines to increase bond strength and heat resistance.