- L-3369 was designed for topcoat applications on a wide variety of substrates, including concrete, metal, plastic and wood.
- L-3369 produces glossy films with excellent leveling properties and good stain- and chemical-resistance to a variety of household food and cleaning products.
- Product Applications
- L-3369 can be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications.
- Rheology modifications can be made with associative thickeners for alternative application methods.
Properties
- Physical Form
- Physical Properties
- Mechanical Properties (TPE)
Value | Units | Test Method / Conditions | |
Solids | 34 - 36 | % | — |
Viscosity | 50 - 200 | cps | — |
pH | 8.5 - 10.0 | — | — |
Density | 8.7 | lbs/gal | — |
VOC Content (less water) | 75 | gm/l | — |
VOC Content (as supplied) | 26 | gm/l | — |
Value | Units | Test Method / Conditions | |
Elongation | 300 | % | Tested at 2 inches/minute |
Tensile Strength | 2700 | psi | Tested at 2 inches/minute |
100% Modulus | 2050 | psi | Tested at 2 inches/minute |
200% Modulus | 2350 | psi | Tested at 2 inches/minute |
Technical Details & Test Data
- Curing
- L-3369 is a film former at 70°F and may be applied at lower temperatures with supplemental co-solvent addition of 3 - 5% hexylene glycol on total formulation weight.
- Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties without additional co-solvent.
- The performance of L-3369-based coatings may be enhanced with carbodiimide and aziridine crosslinkers.
- Drying
- L-3369 is a film former at 70°F and may be applied at lower temperatures with supplemental co-solvent addition of 3 - 5% hexylene glycol on total formulation weight.
- Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties without additional co-solvent.
- The performance of L-3369-based coatings may be enhanced with carbodiimide and aziridine crosslinkers.